Rust is an iron oxide, a usually reddish-brown oxide formed by the reaction of iron and oxygen in the catalytic presence of water or air moisture. Rust consists of hydrous iron (III) oxides (Fe 2 O 3 ·nH 2 O) and iron (III) oxide-hydroxide (FeO (OH), Fe (OH) 3), and is typically associated with the corrosion of refined iron.
Galvanic corrosion. Appearance. Corrosion of an iron nail wrapped in bright copper wire, showing cathodic protection of copper; a ferroxyl indicator solution shows colored chemical indications of two types of ions diffusing through a moist agar medium. Galvanic corrosion (also called bimetallic corrosion or dissimilar metal corrosion) is an ...
v. t. e. Corrosion is a natural process that converts a refined metal into a more chemically stable oxide. It is the gradual deterioration of materials (usually a metal) by chemical or electrochemical reaction with their environment. Corrosion engineering is the field dedicated to controlling and preventing corrosion. [1][2]
Pitting corrosion. Appearance. Severe pitting corrosion problems caused by chloride ions on a truss beam of the Nandu River Iron Bridge (Hainan Province, China) leading to the complete rupture of a metallic element. Pitting corrosion, or pitting, is a form of extremely localized corrosion that leads to the random creation of small holes in metal.
Galvanic series. The galvanic series (or electropotential series) determines the nobility of metals and semi-metals. When two metals are submerged in an electrolyte, while also electrically connected by some external conductor, the less noble (base) will experience galvanic corrosion. The rate of corrosion is determined by the electrolyte, the ...
Bluing, sometimes spelled as blueing, is a passivation process in which steel is partially protected against rust using a black oxide coating. It is named after the blue-black appearance of the resulting protective finish. Bluing involves an electrochemical conversion coating resulting from an oxidizing chemical reaction with iron on the ...
Weathering steel, often referred to by the genericised trademark COR-TEN steel and sometimes written without the hyphen as corten steel, is a group of steel alloys which were developed to eliminate the need for painting by forming a stable external layer of rust. U.S. Steel (USS) holds the registered trademark on the name COR-TEN. [1]
Oxide jacking. The expansive force of rusting, which may be called oxide jacking or rust burst, is a phenomenon that can cause damage to structures made of stone, masonry, concrete or ceramics, and reinforced with metal components. A definition is "the displacement of building elements due to the expansion of iron and steel products as the ...