A variety of hardness-testing methods are available, including the Vickers, Brinell, Rockwell, Meyer and Leeb tests. Although it is impossible in many cases to give an exact conversion, it is possible to give an approximate material-specific comparison table for steels.
BHN = Brinell Hardness Number (kgf/mm 2) P = applied load in kilogram-force (kgf) D = diameter of indenter (mm) d = diameter of indentation (mm) Brinell hardness is sometimes quoted in megapascals; the Brinell hardness number is multiplied by the acceleration due to gravity, 9.80665 m/s 2, to convert it to megapascals.
Vickers hardness test; Brinell scale This page was last edited on 16 November 2024, at 12:16 (UTC). Text is available under the Creative Commons ...
A Rockwell hardness tester. The Rockwell scale is a hardness scale based on indentation hardness of a material. The Rockwell test measures the depth of penetration of an indenter under a large load (major load) compared to the penetration made by a preload (minor load). [1]
When testing coatings, scratch hardness refers to the force necessary to cut through the film to the substrate. The most common test is Mohs scale, which is used in mineralogy. One tool to make this measurement is the sclerometer. Another tool used to make these tests is the pocket hardness tester. This tool consists of a scale arm with ...
Brinell hardness test (HB) BHN and HBW are widely used [7] Knoop hardness test (HK), for measurement over small areas, widely used to test glass or ceramic material. [8] Janka hardness test, for wood; Meyer hardness test; Rockwell hardness test (HR), principally used in the USA. HRA, HRB and HRC scales are most widely used. [9]
Scratch hardness. The Mohs scale of mineral hardness; The Vickers hardness test; The Brinell scale; The Janka hardness test; The Rockwell scale; The Durometer scale; The Barcol scale; The Leeb rebound hardness scale; The Rosiwal scale; The Meyer hardness test; The Knoop hardness test
This is similar to using various indenter geometries and test loads in Rockwell (e.g. HRA, HRB, HRC), Brinell and Vickers. Equotip hardness results in HLx are often converted to the traditional hardness scales HRC, HB and HV mainly for convention reasons between supplier and customer. [5] [6]