Spray forming offers certain advantages over both conventional ingot metallurgy and more specialized techniques such as powder metallurgy.Firstly, it is a flexible process and can be used to manufacture a wide range of materials, some of which are difficult to produce by other methods, e.g. Al-5wt% Li alloys or Al-SiC, Al-Al 2 O 3 metal matrix composites (MMCs).
Thermal spraying can provide thick coatings (approx. thickness range is 20 microns to several mm, depending on the process and feedstock), over a large area at high deposition rate as compared to other coating processes such as electroplating, physical and chemical vapor deposition. Coating materials available for thermal spraying include ...
It is used for spraying pure metal powders with the sizes of 5–50 μm. In low-pressure cold spraying (LPCS), the working gas is a compressed gas with pressure 0.5–1.0 MPa, flow rate 0.5–2 m 3 /min and the heating power 3–5 kW. It is used for spraying a mechanical mixture of metal and ceramic powders.
Cold sprayable metal technology is a metallizing process that seamlessly applies cold sprayable or putty able metal to almost any surface. The composite metal consists of two (water-based binder) or three different ingredients: metal powder, binder and hardener. The mixture of the ingredients is cast or sprayed on the substrate at room temperature.
This graphite layer is then thought to form metastable M 3 C species (where M is the metal), which migrate away from the metal surface. However, in some regimes no M 3 C species are observed indicating a direct transfer of metal atoms into the graphite layer. [2] The temperatures normally associated with metal dusting are high (300–850 °C). [2]
Solution precursor plasma spray (SPPS) is a thermal spray process where a feedstock solution is heated and then deposited onto a substrate. Basic properties of the process are fundamentally similar to other plasma spraying processes. However, instead of injecting a powder into the plasma plume, a liquid precursor is used.
After a surface has been abrasion blasted and/or machined a thin layer of molybdenum, nickel-chromium alloys or nickel aluminide can be spayed before the final detonation spray coating to improve the bond strength. This is known as a bond coating. Bond coatings are often used when spray coating materials of ceramic composites are being applied.
Chemical Bath Deposition has a long history but until recently was an uncommon method of thin-film deposition. [1]In 1865, Justus Liebig published an article describing the use of Chemical Bath Deposition to silver mirrors (to affix a reflective layer of silver to the back of glass to form a mirror), [5] though in the modern day electroplating and vacuum deposition are more common.