Typical material properties for 6005A aluminum alloy include: [2] Density: 2.71 g/cm 3, or 169 lb/ft 3. Electrical Conductivity: 47 to 50% IACS. Young's modulus: 70 GPa, or 10 Msi. Ultimate tensile strength: 190 to 300 MPa, or 28 to 44 ksi. Yield strength: 100 to 260 MPa, or 15 to 38 ksi. Thermal Conductivity: 180 to 190 W/m-K.
The ultimate tensile strength of a material is an intensive property; therefore its value does not depend on the size of the test specimen.However, depending on the material, it may be dependent on other factors, such as the preparation of the specimen, the presence or otherwise of surface defects, and the temperature of the test environment and material.
The aluminium-copper alloys have high strength, but are generally less corrosion resistant and harder to weld than other types of aluminium alloys. To compensate for the lower corrosion resistance, 2219 aluminium can be clad in a commercially pure alloy such as 1050 or painted.
Unhardened 5086 has a yield strength of 120 MPa (17 ksi) and ultimate tensile strength of 260 MPa (38 ksi) from −28 to 100 °C (−18 to 212 °F). At cryogenic temperatures it is slightly stronger: at −196 °C (−321 °F), yield of 130 MPa (19 ksi) and ultimate tensile strength of 380 MPa (55 ksi); above 100 °C (212 °F) its strength is reduced.
The term material strength is used when referring to mechanical stress parameters. These are physical quantities with dimension homogeneous to pressure and force per unit surface. The traditional measure unit for strength are therefore MPa in the International System of Units, and the psi between the United States customary units. Strength ...
For deep draw and complex shapes, and for the avoidance of spring-back, an aluminium hot stamping process (Hot Form Quench) can be used, which forms a blank at a elevated temperature (~ 550 C) in a cooled die, leaving a part in W-temper condition before artificial aging to the T6 full strength state.
Alloy 5083 retains exceptional strength after welding. It has the highest strength of the non-heat treatable alloys with an Ultimate Tensile Strength of 317 MPa or 46000 psi and a Tensile Yield Strength of 228 MPa or 33000 psi. It is not recommended for use in temperatures in excess of 65 °C. [2]
T5 temper 6063 has an ultimate tensile strength of at least 140 MPa (20,000 psi) in thicknesses up to 13 millimetres (0.5 in), and 130 MPa (19,000 psi) from 13 mm (0.5 in) thick, and yield strength of at least 97 MPa (14,000 psi) up to 13 millimetres (0.5 in) and 90 MPa (13,000 psi) from13 to 25 mm (0.5 to 1 in).