For deep draw and complex shapes, and for the avoidance of spring-back, an aluminium hot stamping process (Hot Form Quench) can be used, which forms a blank at a elevated temperature (~ 550 C) in a cooled die, leaving a part in W-temper condition before artificial aging to the T6 full strength state.
T5 temper 6063 has an ultimate tensile strength of at least 140 MPa (20,000 psi) in thicknesses up to 13 millimetres (0.5 in), and 130 MPa (19,000 psi) from 13 mm (0.5 in) thick, and yield strength of at least 97 MPa (14,000 psi) up to 13 millimetres (0.5 in) and 90 MPa (13,000 psi) from13 to 25 mm (0.5 to 1 in).
7068-T6511 has typical ultimate tensile strength of 710 MPa (103 ksi) versus a similar product produced from 7075-T6511 that would have a typical ultimate tensile strength of 640 MPa (93 ksi). Typical yield strength for alloy 7068-T6511 is 683 MPa (99.1 ksi) versus 590 MPa (86 ksi) for a similar product produced from 7075-T6511. [2]
6082 aluminium alloy is an alloy in the wrought aluminium-magnesium-silicon family (6000 or 6xxx series). It is one of the more popular alloys in its series (alongside alloys 6005, 6061, and 6063), although it is not strongly featured in ASTM (North American) standards.
Y alloy; Hiduminium alloys, also known as R.R. alloys: pre-war nickel–aluminium alloys, used in aerospace and engine pistons, for their ability to retain strength at elevated temperature. These are replaced nowadays by higher-performing iron-aluminium alloys like 8009 capable of operating with low creep up to 300 °C.
Unhardened 5086 has a yield strength of 120 MPa (17 ksi) and ultimate tensile strength of 260 MPa (38 ksi) from −28 to 100 °C (−18 to 212 °F). At cryogenic temperatures it is slightly stronger: at −196 °C (−321 °F), yield of 130 MPa (19 ksi) and ultimate tensile strength of 380 MPa (55 ksi); above 100 °C (212 °F) its strength is reduced.
The aluminium-copper alloys have high strength, but are generally less corrosion resistant and harder to weld than other types of aluminium alloys. To compensate for the lower corrosion resistance, 2219 aluminium can be clad in a commercially pure alloy such as 1050 or painted.
Aluminum: 97.3 Silicon: 1 Magnesium: 0.80 Manganese: 0.5 Copper: 0.35 Mechanical Properties. Properties [1] Metric Tensile strength 290 MPa Yield strength ...