The onset of thermal degradation dictates the maximum temperature at which a polymer can be used. It is an important limitation in how the polymer is manufactured and processed. For instance, polymers become less viscous at higher temperatures which makes injection moulding easier and faster, but thermal degradation places a ceiling temperature ...
This interferes with crystallization and lowers the polymer's melting temperature. In general, such PET is known as PETG or PET-G (polyethylene terephthalate glycol-modified). It is a clear amorphous thermoplastic that can be injection-molded, sheet-extruded or extruded as filament for 3D printing .
Glass Transition Temperature: 82 °C (180 °F) [5] Melting point ... gives the polymer very different properties ... operating temperature around 60 °C (140 °F ...
Polybenzimidazole (PBI, short for poly[2,2’-(m-phenylen)-5,5’-bisbenzimidazole]) fiber is a synthetic fiber with a very high decomposition temperature. It does not exhibit a melting point, it has exceptional thermal and chemical stability, and it does not readily ignite. [1]
PTFE is a thermoplastic polymer, which is a white solid at room temperature, with a density of about 2200 kg/m 3 and a melting point of 600 K (327 °C; 620 °F). [27] It maintains high strength, toughness and self-lubrication at low temperatures down to 5 K (−268.2 °C; −450.7 °F), and good flexibility at temperatures above 194 K (−79.15 ...
Perfectly isotactic PP has a melting point of 171 °C (340 °F). Commercial isotactic PP has a melting point that ranges from 160 to 166 °C (320 to 331 °F), depending on atactic material and crystallinity. Syndiotactic PP with a crystallinity of 30% has a melting point of 130 °C (266 °F). [8] Below 0 °C, PP becomes brittle. [9]
Polycaprolactone (PCL) is a synthetic, semi-crystalline, biodegradable polyester with a melting point of about 60 °C and a glass transition temperature of about −60 °C. [2] [3] The most common use of polycaprolactone is in the production of speciality polyurethanes.
The melting point for average commercial low-density polyethylene is typically 105 to 115 °C (221 to 239 °F). These temperatures vary strongly with the type of polyethylene, but the theoretical upper limit of melting of polyethylene is reported to be 144 to 146 °C (291 to 295 °F).