In mathematical terms, failure theory is expressed in the form of various failure criteria which are valid for specific materials. Failure criteria are functions in stress or strain space which separate "failed" states from "unfailed" states. A precise physical definition of a "failed" state is not easily quantified and several working ...
The Tsai–Wu failure criterion is a phenomenological material failure theory which is widely used for anisotropic composite materials which have different strengths in tension and compression. [1] The Tsai-Wu criterion predicts failure when the failure index in a laminate reaches 1.
The Christensen failure criterion is a material failure theory for isotropic materials that attempts to span the range from ductile to brittle materials. [1] It has a two-property form calibrated by the uniaxial tensile and compressive strengths T ( σ T ) {\displaystyle \left(\sigma _{T}\right)} and C ( σ C ) {\displaystyle \left(\sigma _{C ...
Since no material will have this ratio precisely, in practice it is necessary to use engineering judgement to decide what failure theory is appropriate for a given material. Alternately, for use of the Tresca theory, the same ratio is defined as 1/2.
The T-failure criterion is a set of material failure criteria that can be used to predict both brittle and ductile failure. [1] [2]These criteria were designed as a replacement for the von Mises yield criterion which predicts the unphysical result that pure hydrostatic tensile loading of metals never leads to failure.
Hierarchy of micromechanics-based analysis procedure for composite structures. The theory of micro-mechanics of failure aims to explain the failure of continuous fiber reinforced composites by micro-scale analysis of stresses within each constituent material (such as fiber and matrix), and of the stresses at the interfaces between those constituents, calculated from the macro stresses at the ...
The Tsai hill criterion is interactive, i.e. the stresses in different directions are not decoupled and do affect the failure simultaneously. [2] Furthermore, it is a failure mode independent criterion, as it does not predict the way in which the material will fail, as opposed to mode-dependent criteria such as the Hashin criterion, or the Puck ...
The Drucker–Prager yield criterion [1] is a pressure-dependent model for determining whether a material has failed or undergone plastic yielding. The criterion was introduced to deal with the plastic deformation of soils. It and its many variants have been applied to rock, concrete, polymers, foams, and other pressure-dependent materials.