6061-T6 aluminium standard heat treating process. T6 temper 6061 has been treated to provide the maximum precipitation hardening (and therefore maximum yield strength) for a 6061 aluminium alloy. It has an ultimate tensile strength of at least 290 MPa (42 ksi) and yield strength of at least 240 MPa (35 ksi).
Recommended for 300-series stainless steel. Good for food-handling applications with close joint tolerances. Gap 0.1–0.25 mm. Alloy specifically designed for brazing tungsten carbide tips to steel tools and wear parts. Readily wets nickel and iron alloys. Nickel offsets embrittlement by aluminium diffusion when brazing aluminium bronzes.
Note that the term aircraft aluminium or aerospace aluminium usually refers to 7075. [65] [66] 4047 aluminium is a unique alloy used in both the aerospace and automotive applications as a cladding alloy or filler material. As filler, aluminium alloy 4047 strips can be combined to intricate applications to bond two metals. [67]
T1 temper 6063 has an ultimate tensile strength of at least 120 MPa (17,000 psi) in thicknesses up to 12.7 mm (0.5 in), and 110 MPa (16,000 psi) from 13 to 25 mm (0.5 to 1 in) thick, and yield strength of at least 62 MPa (9,000 psi) in thickness up to 13 millimetres (0.5 in) and 55 MPa (8,000 psi) from 13 mm (0.5 in) thick.
T6 temper 7075 has an ultimate tensile strength of 510–540 MPa (74,000–78,000 psi) and yield strength of at least 430–480 MPa (63,000–69,000 psi). It has a failure elongation of 5–11%. [9] The T6 temper is usually achieved by homogenizing the cast 7075 at 450 °C for several hours, quenching, and then ageing at 120 °C for 24 hours.
6082 aluminium alloy is an alloy in the wrought aluminium-magnesium-silicon family (6000 or 6xxx series). It is one of the more popular alloys in its series (alongside alloys 6005 , 6061 , and 6063 ), although it is not strongly featured in ASTM (North American) standards.
Aluminium–scandium alloys (AlSc) are aluminum alloys that consist largely of aluminium (Al) and traces of scandium (Sc) as the main alloying elements.In principle, aluminium alloys strengthened with additions of scandium are very similar to traditional nickel-base superalloys in that both are strengthened by coherent, coarsening resistant precipitates with an ordered L1 2 structure.
By comparison, annealed type 316 stainless steel has a density of 8000 kg/m 3, modulus of 193 GPa, and tensile strength of 570 MPa. [23] Tempered 6061 aluminium alloy has a density of 2700 kg/m 3, modulus of 69 GPa, and tensile strength of 310 MPa, respectively. [24] Ti-6Al-4V standard specifications include: [25] [26]