A metallurgical furnace, often simply referred to as a furnace when the context is known, is an industrial furnace used to heat, melt, or otherwise process metals. Furnaces have been a central piece of equipment throughout the history of metallurgy ; processing metals with heat is even its own engineering specialty known as pyrometallurgy .
Typically a transfer ladle will be used to transfer molten metal from a primary melting furnace to either a holding furnace or an auto-pour unit. Treatment ladle: a ladle used for a process to take place within the ladle to change some aspect of the molten metal. A typical example being to convert cast iron to ductile iron by the addition of ...
The maximum melting area of day tanks is 10 m2, and the melting capacity is between 0.4 and 0.8 t/m2 of melting area. The pot furnace is one type of this. The furnace consists of a refractory masonry basin with a depth of 40 to 60 cm (bottom furnace), which is covered with a vault with a diameter of 70 to 80 cm (top furnace).
A cupola or cupola furnace is a melting device used in foundries that can be used to melt cast iron, Ni-resist iron and some bronzes. The cupola can be made almost any practical size. The size of a cupola is expressed in diameters and can range from 1.5 to 13 feet (0.5 to 4.0 m). [1]
The advantage of the induction furnace is a clean, energy-efficient and well-controlled melting process, compared to most other means of metal melting. Most modern foundries use this type of furnace, and many iron foundries are replacing cupola furnaces with induction furnaces to melt cast iron, as the former emit much dust and other pollutants ...
An electron-beam furnace (EB furnace) is a type of vacuum furnace employing high-energy electron beam in vacuum as the means for delivery of heat to the material being melted. It is one of the electron-beam technologies .
Vacuum arc remelting (VAR) is a secondary melting process for production of metal ingots with elevated chemical and mechanical homogeneity for highly demanding applications. [1] The VAR process has revolutionized the specialty traditional metallurgical techniques industry, and has made possible tightly controlled materials used in biomedical ...
Zinc is not miscible with lead and when the two molten metals are mixed, the zinc separates and floats to the top with ~2% lead. However, silver dissolves more easily in zinc, so the upper layer of zinc carries a significant portion of the silver. The melt is then cooled until the zinc solidifies and the dross is skimmed off.