This type of material is non-rigid, and is sometimes called TPR for ThermoPlastic Rubber. To increase the rigidity of a TPO blend, fillers exploit a surface tension phenomena. By selecting a filler with a higher surface area per weight, a higher flexural modulus can be achieved. Specific density of TPO blends range from 0.92 to 1.1.
Poly(p-phenylene oxide) (PPO), poly(p-phenylene ether) (PPE), poly(oxy-2,6-dimethyl-1,4-phenylene), often referred to simply as polyphenylene oxide, is a high-temperature thermoplastic with the general formula (C 8 H 8 O) n. It is rarely used in its pure form due to difficulties in processing.
Thermoplastic olefins (TPO) are increasingly used as a roofing material. [8] TPEs are also widely used for catheters where nylon block copolymers offer a range of softness ideal for patients. Thermoplastic silicone and olefin blends are used for extrusion of glass run and dynamic weatherstripping car profiles.
A polyolefin is a type of polymer with the general formula (CH 2 CHR) n where R is an alkyl group. They are usually derived from a small set of simple olefins . Dominant in a commercial sense are polyethylene and polypropylene. More specialized polyolefins include polyisobutylene and polymethylpentene. They are all colorless or white oils or ...
HDPE is known for its high strength-to-density ratio. [4] The density of HDPE ranges from 930 to 970 kg/m 3. [5] Although the density of HDPE is only marginally higher than that of low-density polyethylene, HDPE has little branching, giving it stronger intermolecular forces and tensile strength (38 MPa versus 21 MPa) than LDPE. [6]
Triphenylphosphine oxide (often abbreviated TPPO) is the organophosphorus compound with the formula OP(C 6 H 5) 3, also written as Ph 3 PO or PPh 3 O (Ph = C 6 H 5). It is one of the more common phosphine oxides. This colourless crystalline compound is a common but potentially useful waste product in reactions involving triphenylphosphine.
LDPE has SPI resin ID code 4 Schematic of LDPE branching structure. Low-density polyethylene (LDPE) is a thermoplastic made from the monomer ethylene.It was the first grade of polyethylene, produced in 1933 by John C. Swallow and M.W Perrin who were working for Imperial Chemical Industries (ICI) using a high pressure process via free radical polymerization. [1]
Chemical formula. C 15 H 20 O 6: Molar mass ... Molar mass: 296.319 g·mol −1 Density: 1.06 Except where otherwise noted, data are given for materials in their ...