Degraded concrete and rusted, exposed reinforcement bar (rebar) on Welland River bridge of the Queen Elizabeth Way in Niagara Falls, Ontario. Concrete degradation may have many different causes. Concrete is mostly damaged by the corrosion of reinforcement bars due to the carbonatation of hardened cement paste or chloride attack under wet ...
On the other hand, for completely dry concrete, the chemical reaction of carbonation cannot occur. Another influencing factor for CO 2 diffusion rate is concrete porosity. Concrete obtained with higher w/c ratio or obtained with an incorrect curing process presents higher porosity at hardened state, and is therefore subjected to a higher ...
Calcium aluminates can form complex salts in combination with different types of anions.Two series of calcium aluminates are known in cement chemistry: AFm and AFt phases, being respectively mono- or tri-substituted with a given divalent anion X (e.g. SO 2− 4, CO 2− 3, or hosting a divalent impurity such as SeO 2− 4 [3]...), or with two units of a monovalent anion, e.g. OH −, Cl − ...
Concrete degradation; S. Sulfate attack in concrete and mortar This page was last edited on 29 September 2024, at 15:37 (UTC). Text is available under the Creative ...
ASTM C1293: "Test Method for Concrete Aggregates by Determination of Length Change of Concrete Due to Alkali-Silica Reaction". It is a long-term confirmation test (1 or 2 years) at 38 °C in a water-saturated moist atmosphere (inside a thermostated oven) with concrete prisms containing the aggregates to be characterised mixed with a high-alkali ...
Robotic Hydrodemolition in Folkestone, UK. Hydrodemolition of concrete exposing the rebar.. Hydrodemolition (also known as hydro demolition, hydroblasting, hydro blasting, hydromilling, waterblasting, and waterjetting) is a concrete removal technique which utilizes high-pressure water, often containing an abrasive material, to remove deteriorated and sound concrete as well as asphalt and grout.
Oxide jacking has caused concrete spalling on walls of the Herbst Pavilion at Fort Mason Center in San Francisco. The expansive force of rusting, which may be called oxide jacking or rust burst, is a phenomenon that can cause damage to structures made of stone, masonry, concrete or ceramics, and reinforced with metal components.
A fairly well-defined reaction front can often be observed in thin sections; ahead of the front the concrete is normal, or near normal. Behind the reaction front, the composition and the microstructure of concrete are modified. These changes may vary in type or severity but commonly include: Extensive cracking; Expansion