4043 aluminium alloy [1] [2] [3] is a wrought aluminium alloy with good corrosion resistance typically used as filler material [4] [5] for welding of aluminium parts. It contains high amounts of silicon (between 4.5 and 6%) and trace amounts of other metals. [6]
Unhardened 5086 has a yield strength of 120 MPa (17 ksi) and ultimate tensile strength of 260 MPa (38 ksi) from −28 to 100 °C (−18 to 212 °F). At cryogenic temperatures it is slightly stronger: at −196 °C (−321 °F), yield of 130 MPa (19 ksi) and ultimate tensile strength of 380 MPa (55 ksi); above 100 °C (212 °F) its strength is reduced.
5754 aluminium–magnesium alloy is an alloy in the wrought aluminium -magnesium family (5000 or 5xxx series). It is closely related to the alloys 5154 and 5454 (Aluminum Association designations that only differ in the second digit are variations on the same alloy).
6061 aluminium alloy (Unified Numbering System (UNS) designation A96061) is a precipitation-hardened aluminium alloy, containing magnesium and silicon as its major alloying elements.
Aluminum-silicon phase diagram. Aluminum forms a eutectic with silicon, which is at 577 °C, with a Si content of 12.5% [7] or 12.6%. [8] Up to 1.65% Si can be dissolved in aluminum at this temperature. However, the solubility decreases rapidly with temperature. At 500 °C it is still 0.8% Si, at 400 °C 0.3% Si and at 250 °C only 0.05% Si.
Heroes don’t always wear capes — sometimes they’re covered in venom … at least if you’re Tom Hardy.. The actor, 47, reportedly offered to pay £250,000 — or approximately $315,000 ...
My heart! At the end when they were sleeping with her, I totally melted! This brought back so many memories for me of bringing home our babies and our Westies meeting them for the first time.
5083 aluminium alloy is an aluminium–magnesium alloy with magnesium and traces of manganese and chromium. It is highly resistant to attack by seawater and industrial chemicals.