Metallography allows the metallurgist to study the microstructure of metals. A micrograph of bronze revealing a cast dendritic structure Al-Si microstructure. Microstructure is the very small scale structure of a material, defined as the structure of a prepared surface of material as revealed by an optical microscope above 25× magnification. [1]
This microstructure is advantageous over other microstructures for steel because of its chaotic ordering, which increases toughness. [ 1 ] Acicular ferrite is formed in the interior of the original austenitic grains by direct nucleation on the inclusions, resulting in randomly oriented short ferrite needles with a 'basket weave' appearance.
Bainite is a plate-like microstructure that forms in steels at temperatures of 125–550 °C (depending on alloy content). [1] First described by E. S. Davenport and Edgar Bain, [2] [3] it is one of the products that may form when austenite (the face-centered cubic crystal structure of iron) is cooled past a temperature where it is no longer thermodynamically stable with respect to ferrite ...
Metallurgy derives from the Ancient Greek μεταλλουργός, metallourgós, "worker in metal", from μέταλλον, métallon, "mine, metal" + ἔργον, érgon, "work" The word was originally an alchemist's term for the extraction of metals from minerals, the ending -urgy signifying a process, especially manufacturing: it was discussed in this sense in the 1797 Encyclopædia ...
The properties of steel depend on its microstructure: the arrangement of different phases, some harder, some with greater ductility. At the atomic level, the four phases of auto steel include martensite (the hardest yet most brittle), bainite (less hard), ferrite (more ductile), and austenite (the most ductile). The phases are arranged by ...
Pearlite is a microstructure occurring in many common grades of steels. ... of carbon and other alloy elements like silicon and ... steel can in principle be ...
Iron is always the main element in steel, but many other elements may be present or added. Stainless steels, which are resistant to corrosion and oxidation, typically are 11% chromium. Iron is the base metal of steel. Depending on the temperature, it can take two crystalline forms (allotropic forms): body-centred cubic and face-centred cubic.
For a eutectoid steel (0.76% C), between 6 and 10% of austenite, called retained austenite, will remain. The percentage of retained austenite increases from insignificant for less than 0.6% C steel, to 13% retained austenite at 0.95% C and 30–47% retained austenite for a 1.4% carbon steel. A very rapid quench is essential to create martensite.