Nevertheless, anatase is often the first titanium dioxide phase to form in many processes due to its lower surface energy, with a transformation to rutile taking place at elevated temperatures. [7] Although the degree of symmetry is the same for both anatase and rutile phases, there is no relation between the interfacial angles of the two ...
Rutile is an oxide mineral composed of titanium dioxide (TiO 2), the most common natural form of TiO 2. Rarer polymorphs of TiO 2 are known, including anatase, akaogiite, and brookite. Rutile has one of the highest refractive indices at visible wavelengths of any known crystal and also exhibits a particularly large birefringence and high ...
Rutile is the next most abundant and contains around 98% titanium dioxide in the ore. The metastable anatase and brookite phases convert irreversibly to the equilibrium rutile phase upon heating above temperatures in the range 600–800 °C (1,110–1,470 °F). [14]
Ultrafine anatase form is precipitated from sulfate solution and ultrafine rutile from chloride solution. In the chloride process, natural or synthetic rutile is chlorinated at temperatures of 850–1000 °C, and the titanium tetrachloride is converted to the ultrafine anatase form by vapor-phase oxidation. [6]: 1–2
This is the case for anatase, a metastable polymorph of titanium dioxide, which despite commonly being the first phase to form in many synthesis processes due to its lower surface energy, is always metastable, with rutile being the most stable phase at all temperatures and pressures. [1]
This is notably the case for the anatase polymorph of titanium dioxide, which having a lower surface energy is commonly the first phase to form by crystallisation from amorphous precursors or solutions despite being metastable, with rutile being the equilibrium phase at all temperatures and pressures. [4]
Phase transitions (phase changes) that help describe polymorphism include polymorphic transitions as well as melting and vaporization transitions. According to IUPAC, a polymorphic transition is "A reversible transition of a solid crystalline phase at a certain temperature and pressure (the inversion point) to another phase of the same chemical composition with a different crystal structure."
Phase stability reversal of bulk (macroscopic) particles at small sizes. Usually, a less stable bulk-phase at low temperature (and/or low pressure) becomes more stable than the bulk-stable phase as the particle size decreases below a certain critical size. For instance, bulk anatase (TiO 2) is metastable with respect to bulk rutile (TiO 2).