Different forms and tempers of 6061 aluminium alloy are discussed in the following standards: [28] ASTM B209: Standard Specification for Aluminum and Aluminum-Alloy Sheet and Plate; ASTM B210: Standard Specification for Aluminum and Aluminum-Alloy Drawn Seamless Tubes; ASTM B211: Standard Specification for Aluminum and Aluminum-Alloy Bar, Rod ...
The AlMgSi alloys are therefore understood in the standards as a separate group (6000 series) and not as a subgroup of aluminum-magnesium alloys that cannot be hardenable. AlMgSi is one of the aluminum alloys with medium to high strength, high fracture resistance, good welding suitability, corrosion resistance and formability. They can be ...
The high temperature of annealing may result in oxidation of the metal's surface, resulting in scale. If scale must be avoided, annealing is carried out in a special atmosphere, such as with endothermic gas (a mixture of carbon monoxide, hydrogen gas, and nitrogen gas). Annealing is also done in forming gas, a mixture of hydrogen and nitrogen.
By comparison, annealed type 316 stainless steel has a density of 8000 kg/m 3, modulus of 193 GPa, and tensile strength of 570 MPa. [23] Tempered 6061 aluminium alloy has a density of 2700 kg/m 3, modulus of 69 GPa, and tensile strength of 310 MPa, respectively. [24] Ti-6Al-4V standard specifications include: [25] [26]
In general, stiffer and lighter designs can be achieved with aluminium alloy than is feasible with steels. For instance, consider the bending of a thin-walled tube: the second moment of area is inversely related to the stress in the tube wall, i.e. stresses are lower for larger values. The second moment of area is proportional to the cube of ...
Aluminum 6061–O (annealed) 0.20: 205 Aluminum 6061–T6: 0.05: 410 Aluminum 7075–O (annealed) 0.17: 400 Brass, Naval (annealed) 0.49: 895 Brass 70–30 (annealed) 0.49: 900 Brass 85–15 (cold-rolled) 0.34: 580 Cobalt-base alloy (heat-treated) 0.50: 2,070 Copper (annealed) 0.54: 325 AZ-31B magnesium alloy (annealed) 0.16: 450 Low-carbon ...
6082 aluminium alloy is an alloy in the wrought aluminium-magnesium-silicon family (6000 or 6xxx series). It is one of the more popular alloys in its series (alongside alloys 6005, 6061, and 6063), although it is not strongly featured in ASTM (North American) standards.
T1 temper 6063 has an ultimate tensile strength of at least 120 MPa (17,000 psi) in thicknesses up to 12.7 mm (0.5 in), and 110 MPa (16,000 psi) from 13 to 25 mm (0.5 to 1 in) thick, and yield strength of at least 62 MPa (9,000 psi) in thickness up to 13 millimetres (0.5 in) and 55 MPa (8,000 psi) from 13 mm (0.5 in) thick.