Dyneema Composite Fabric (DCF), also known as Cuben Fiber (CTF3), is a high-performance non-woven composite material used in high-strength, low-weight applications. It is constructed from a thin sheet of ultra-high-molecular-weight polyethylene ( UHMWPE , "Dyneema") laminated between two sheets of polyester .
Dyneema and Spectra are brands of lightweight high-strength oriented-strand gels spun through a spinneret. They have yield strengths as high as 2.4 GPa (350,000 psi) and density as low as 0.97 g/mL (0.035 lb/cu in) (for Dyneema SK75). [ 12 ]
The first paragraph in the applications section notes that the Dyneema and Spectra products have a strength which is comparable to high strength steel. This is an overstatement since, if in reference to: SAE High-Strength Low-Alloy (HSLA), or ASTM A490 (High strength structural bolts)
It is also known as the strength-to-weight ratio or strength/weight ratio or strength-to-mass ratio. In fiber or textile applications, tenacity is the usual measure of specific strength. The SI unit for specific strength is Pa ⋅ m 3 / kg , or N ⋅m/kg, which is dimensionally equivalent to m 2 /s 2 , though the latter form is rarely used.
M5 has a tensile strength of 4 GPa [1] to 9.5GPa. [2] Other aramids- (such as Kevlar and Twaron) or UHMWPE-fibres (such as Dyneema and Spectra) range from 2.2 to 3.9 GPa. [3]M5 has "very high levels" of fire resistance, flame retardancy, and chemical resistance, especially high for an organic fiber.
Webbing is also made from exceptionally high-strength material, such as Dyneema, and Kevlar. Webbing is both light and strong, with breaking strengths readily available in excess of 10,000 pounds-force (44 kilonewtons). [1] There are two basic constructions of webbing.
The ultimate tensile strength of a material is an intensive property; therefore its value does not depend on the size of the test specimen.However, depending on the material, it may be dependent on other factors, such as the preparation of the specimen, the presence or otherwise of surface defects, and the temperature of the test environment and material.