With body-centered cubic materials (bcc), the Wöhler curve often becomes a horizontal line with decreasing stress amplitude, i.e. there is a fatigue strength that can be assigned to these materials. With face-centered cubic metals (fcc), the Wöhler curve generally drops continuously, so that only a fatigue limit can be assigned to these ...
Where materials do not have a distinct limit the term fatigue strength or endurance strength is used and is defined as the maximum value of completely reversed bending stress that a material can withstand for a specified number of cycles without a fatigue failure. [3] [4] For polymeric materials, the fatigue limit is also commonly known as the ...
Vibration fatigue is a mechanical engineering term describing material fatigue, caused by forced vibration of random nature. An excited structure responds according to its natural-dynamics modes, which results in a dynamic stress load in the material points. [ 1 ]
Within the branch of materials science known as material failure theory, the Goodman relation (also called a Goodman diagram, a Goodman-Haigh diagram, a Haigh diagram or a Haigh-Soderberg diagram) is an equation used to quantify the interaction of mean and alternating stresses on the fatigue life of a material. [1]
The effects of corrosive environments on the fatigue behavior of metals were studied as early as 1930. [1] The phenomenon should not be confused with stress corrosion cracking, where corrosion (such as pitting) leads to the development of brittle cracks, growth and failure. The only requirement for corrosion fatigue is that the sample be under ...
With static fatigue materials experience damage or failure under stress levels that are lower than their normal ultimate tensile strengths. [2] The exact details vary with the material type and environmental factors, such as moisture presence [3] and temperature. [4] [5] This phenomenon is closely related to stress corrosion cracking. [1]
In materials science, material failure is the loss of load carrying capacity of a material unit. This definition introduces to the fact that material failure can be examined in different scales, from microscopic, to macroscopic. In structural problems, where the structural response may be beyond the initiation of nonlinear material behaviour ...
The wing was tested for a total of 47500 flights which is 2.5 times the number of flights in 25 years of operation. Each 16 hour flight took 11 minutes to simulate on the fatigue test rig. [3] Fatigue testing is a specialised form of mechanical testing that is performed by applying cyclic loading to a coupon or structure.