Cement board is composed of aggregated Portland cement with a glass-fiber mesh on the surfaces. This 5 ⁄ 16 inch (7.9 mm) thick cement board is designed as an underlayment for tile floors.
Magnesium oxide wallboard (10 mm thickness) Magnesium oxide, more commonly called magnesia, is a mineral that when used as part of a cement mixture and cast into thin cement panels under proper curing procedures and practices can be used in residential and commercial building construction.
Homasote is a brand name associated with the product generically known as cellulose-based fiber wall board, which is similar in composition to papier-mâché, made from recycled paper that is compressed under high temperature and pressure.
Blue fiber cement siding HardiePanel on design-build addition, Ithaca NY. Fiber cement siding (also known as "fibre cement cladding" in the United Kingdom, "fibro" in Australia, and by the proprietary name "Hardie Plank" in the United States) is a building material used to cover the exterior of a building in both commercial and domestic applications.
Lath seen from the back with white plaster coat oozing through. Lath and plaster is a building process used to finish mainly interior dividing walls and ceilings. It consists of narrow strips of wood which are nailed horizontally across the wall studs or ceiling joists and then coated in plaster.
Backer board may refer to: Cement board used as tile backer board (to support tiles) Cardboard used in the conservation of comic books to keep pages flat
Hardboard is similar to particle board and medium-density fiberboard, but is denser, stronger and harder because it is made out of exploded wood fibers that have been highly compressed.
Closed-cell rod will also lose firmness and out-gas if damaged during installation or overcompressed or at sharp bends. The gasses cannot pass through this backer rod and can deform, weaken, and even cause holes (leaks) in the caulk or sealant as it escapes. Out-gassing is the reason that open-cell backer rod was developed. [7]