Etching is used in microfabrication to chemically remove layers from the surface of a wafer during manufacturing. Etching is a critically important process module in fabrication, and every wafer undergoes many etching steps before it is complete. For many etch steps, part of the wafer is protected from the etchant by a "masking" material which ...
Wet etching was widely used in the 1960s and 1970s, [144] [145] but it was replaced by dry etching/plasma etching starting at the 10 micron to 3 micron nodes. [146] [147] This is because wet etching makes undercuts (etching under mask layers or resist layers with patterns). [148] [149] [150] Dry etching has become the dominant etching technique ...
The hard bake solidifies the remaining photoresist, to make a more durable protecting layer in future ion implantation, wet chemical etching, or plasma etching. From preparation until this step, the photolithography procedure has been carried out by two machines: the photolithography stepper or scanner, and the coater/developer.
Buffered oxide etch (BOE), also known as buffered HF or BHF, is a wet etchant used in microfabrication. It is a mixture of a buffering agent, such as ammonium fluoride NH4F, and hydrofluoric acid (HF). Its primary use is in etching thin films of silicon nitride (Si 3 N 4) or silicon dioxide (SiO 2), by the reaction: SiO2 + 4HF + 2NH4F → (NH4 ...
A reactive-ion etching setup in a laboratory cleanroom. Reactive-ion etching (RIE) is an etching technology used in microfabrication. RIE is a type of dry etching which has different characteristics than wet etching. RIE uses chemically reactive plasma to remove material deposited on wafers. The plasma is generated under low pressure (vacuum ...
Metal Assisted Chemical Etching (also known as MACE) is the process of wet chemical etching of semiconductors (mainly silicon) with the use of a metal catalyst, usually deposited on the surface of a semiconductor in the form of a thin film or nanoparticles. The semiconductor, covered with the metal is then immersed in an etching solution ...
To etch through a 0.5 mm silicon wafer, for example, 100–1000 etch/deposit steps are needed. The two-phase process causes the sidewalls to undulate with an amplitude of about 100–500 nm. The cycle time can be adjusted: short cycles yield smoother walls, and long cycles yield a higher etch rate.
The RCA clean is a standard set of wafer cleaning steps which need to be performed before high-temperature processing steps (oxidation, diffusion, CVD) of silicon wafers in semiconductor manufacturing. Werner Kern developed the basic procedure in 1965 while working for RCA, the Radio Corporation of America. [1][2][3] It involves the following ...