The onset of thermal degradation dictates the maximum temperature at which a polymer can be used. It is an important limitation in how the polymer is manufactured and processed. For instance, polymers become less viscous at higher temperatures which makes injection moulding easier and faster, but thermal degradation places a ceiling temperature ...
Crystallization affects optical, mechanical, thermal and chemical properties of the polymer. The degree of crystallinity is estimated by different analytical methods and it typically ranges between 10 and 80%, with crystallized polymers often called "semi-crystalline". The properties of semi-crystalline polymers are determined not only by the ...
Polymer degradation is the reduction in the physical properties of a polymer, such as strength, caused by changes in its chemical composition. Polymers and particularly plastics are subject to degradation at all stages of their product life cycle , including during their initial processing, use, disposal into the environment and recycling. [ 1 ]
Unlike classical polymer melts, whose flow properties are largely dependent on friction between monomers, vitrimers become a viscoelastic fluid because of exchange reactions at high temperatures as well as monomer friction. [11] These two processes have different activation energies, resulting in a wide
Main chain LCPs have rigid, rod-like mesogens in the polymer backbones, which indirectly leads to the high melting temperature of this kind of LCPs. To make this kind of polymer easy to process, different methods are applied to lower the transition temperature: introducing flexible sequences, introducing bends or kinks, or adding substituent ...
PTFE is a thermoplastic polymer, which is a white solid at room temperature, with a density of about 2200 kg/m 3 and a melting point of 600 K (327 °C; 620 °F). [26] It maintains high strength, toughness and self-lubrication at low temperatures down to 5 K (−268.2 °C; −450.7 °F), and good flexibility at temperatures above 194 K (−79.15 ...
The copolymer Poly(vinylidene fluoride-co-hexafluoropropylene) or PVDF-HFP is used as a co-polymer in the blades of artificial turf. [17] Addition of organoclay to PVDF-HFP via melt compounding stabilizes the β piezoelectric phase. [18] Copolymers of PVDF are also used in piezoelectric and electrostrictive applications.
Although it is thermoplastic, polyacrylonitrile does not melt under normal conditions. It degrades before melting. It melts above 300 °C if the heating rates are 50 degrees per minute or above. [12] Glass transition temperature is around 95 °C and fusion temperature is at 322 °C.