Precipitation hardening (also called age hardening) is a process where a second phase that begins in solid solution with the matrix metal is precipitated out of solution with the metal as it is quenched, leaving particles of that phase distributed throughout to cause resistance to slip dislocations. This is achieved by first heating the metal ...
Precipitation hardening, also called age hardening or particle hardening, is a heat treatment technique used to increase the yield strength of malleable materials, including most structural alloys of aluminium, magnesium, nickel, titanium, and some steels, stainless steels, and duplex stainless steel.
To examine a piece of steel, obtain a hand file and file an edge of the selected metal. If the piece of steel has not undergone the hardening process, the metal file should easily 'bite' into the sample. If the metal has been hardened, the file fails to cut into the sample and glances off with little visible effect.
Here, n is the strain-hardening exponent and K is the strength coefficient. n is a measure of a material's work hardening behavior. Materials with a higher n have a greater resistance to necking. Typically, metals at room temperature have n ranging from 0.02 to 0.5. [3]
Induction heating is a non contact heating process which uses the principle of electromagnetic induction to produce heat inside the surface layer of a work-piece. By placing a conductive material into a strong alternating magnetic field, electric current can be made to flow in the material thereby creating heat due to the I 2 R losses in the material.
Case-hardening or carburization is the process of introducing carbon to the surface of a low-carbon iron, or more commonly a low-carbon steel object, in order to harden the surface. Iron which has a carbon content greater than ~0.02% is known as steel .
Austempering is a hardening process that is used on iron-based metals to promote better mechanical properties. The metal is heated into the austenite region of the iron- cementite phase diagram and then quenched in a salt bath or other heat extraction medium that is between temperatures of 300–375 °C (572–707 °F).
Surface carburizing, or case hardening, is one example of solid solution strengthening in which the density of solute carbon atoms is increased close to the surface of the steel, resulting in a gradient of carbon atoms throughout the material. This provides superior mechanical properties to the surface of the steel without having to use a ...