A variety of hardness-testing methods are available, including the Vickers, Brinell, Rockwell, Meyer and Leeb tests. Although it is impossible in many cases to give an exact conversion, it is possible to give an approximate material-specific comparison table for steels.
Deformation parameters, such as the indentation depth in the Rockwell method, are recorded to give measures of hardness. [ 2 ] According to the dynamic Leeb principle, the hardness value is derived from the energy loss of a defined impact body after impacting on a metal sample, similar to the Shore scleroscope .
The Brinell scale; The Janka hardness test; The Rockwell scale; The Durometer scale; The Barcol scale; The Leeb rebound hardness scale; The Rosiwal scale; The Meyer hardness test; The Knoop hardness test
Brinell hardness is sometimes quoted in megapascals; the Brinell hardness number is multiplied by the acceleration due to gravity, 9.80665 m/s 2, to convert it to megapascals. The Brinell hardness number can be correlated with the ultimate tensile strength (UTS), although the relationship is dependent on the material, and therefore determined ...
The Rockwell scale is a hardness scale based on indentation hardness of a material. The Rockwell test measures the depth of penetration of an indenter under a large load (major load) compared to the penetration made by a preload (minor load). [ 1 ]
This page was last edited on 16 November 2024, at 12:16 (UTC).; Text is available under the Creative Commons Attribution-ShareAlike 4.0 License; additional terms may apply.
Brinell hardness test (HB) BHN and HBW are widely used [7] Knoop hardness test (HK), for measurement over small areas, widely used to test glass or ceramic material. [8] Janka hardness test, for wood; Meyer hardness test; Rockwell hardness test (HR), principally used in the USA. HRA, HRB and HRC scales are most widely used.
Hardness (Brinell scale) Comments Copper (ASTM B1, B2, B3, B152, B124, R133) Cu 99.9 Annealed 10 32 45 42 Electrical equipment, roofing, screens Cold-drawn 40 45 15 90 Cold-rolled 40 46 5 100 Gilding metal (ASTM B36) Cu 95.0, Zn 5.0 Cold-rolled 50 56 5 114 Coins, bullet jackets: Cartridge brass (ASTM B14, B19, B36, B134, B135) Cu 70.0, Zn 30.0