A572 Steel Material Properties, Per ASTM Standards [2]; A572 Grade Yield Point (KSI) [MPa] Tensile Strength (KSI) [MPa] Min. 8” Elongation % Grade 42
Steel grades to classify various steels by their composition and physical ... So S355 has a minimum yield strength of 355 MPa for the smallest thickness range covered ...
ASTM A992 steel has the following minimum mechanical properties, according to ASTM specification A992/A992M. Tensile yield strength, 345 MPa (50 ksi); tensile ultimate strength, 450 MPa (65 ksi); strain to rupture (sometimes called elongation ) in a 200-mm-long test specimen, 18%; strain to rupture in a 50-mm-long test specimen, 21%.
Yield strength (MPa) Ultimate strength (MPa) ASTM A36 steel: 250: 400 Steel, API 5L X65 [2] 448: 531 Steel, high strength alloy ASTM A514: 690: 760 Steel, prestressing strands 1650: 1860 Piano wire 1740–3300 [3] Carbon fiber (CF, CFK) 5650 [4] High-density polyethylene (HDPE) 26–33: 37 Polypropylene: 12–43: 19.7–80 Stainless steel AISI ...
It has a yield strength up to 80,000 psi (550 MPa) but costs only 24% more than A36 steel (36,000 psi (250 MPa)). One of the disadvantages of this steel is that it is 30 to 40% less ductile . In the U.S., these steels are dictated by the ASTM standards A1008/A1008M and A1011/A1011M for sheet metal and A656/A656M for plates.
The 32 grades have yield strength of 45,500 psi (315 MPa), and ultimate tensile strength of 64,000 - 85,000 psi (440-590 MPa). The 36 grades have yield strength of 51,000 psi (355 MPa), and ultimate tensile strength of 71,000 - 90,000 psi (490-620 MPa). Per Steel Vessel Rules Part 2 Chapter 1 Section 3 Table 2 (pg 36).
Spring steel is a name given to a wide range of steels [1] used in the manufacture of different products, including swords, saw blades, springs and many more. These steels are generally low-alloy manganese , medium-carbon steel or high-carbon steel with a very high yield strength .
Volume, modulus of elasticity, distribution of forces, and yield strength affect the impact strength of a material. In order for a material or object to have a high impact strength, the stresses must be distributed evenly throughout the object. It also must have a large volume with a low modulus of elasticity and a high material yield strength. [7]