"Black nickel" is a dark coating that consists primarily of nickel sulfide and metallic zinc and nickel. [14] It is typically plated on brass, bronze, or steel in order to produce a non-reflective surface. [15] This type of plating is used for decorative and military purposes and does not offer much protection. [1] [2] [15]
Black nickel plating was developed around 1905, and between the two wars, black chrome plating (first German patent 1929.GP 607, 420), which saw wider use only from the mid-1950s. [14] After the First World War, the first procedures for anodic oxidation and coloring of anodically oxidized aluminium were developed (1923, 1924.DRP. 413876).
The main ingredients of an electroless nickel plating bath are source of nickel cations Ni 2+, usually nickel sulfate and a suitable reducing agent, such as hypophosphite H 2 PO − 2 or borohydride BH − 4. [1] With hypophosphite, the main reaction that produces the nickel plating yields orthophosphite H 2 PO − 3, elemental phosphorus ...
Brown or black can be used as a base color for copper patina. If the amount of chlorides decreases the color will be more bluish-green, if carbonate decreases, more yellow-green. [27] Black for copper. Solution of sodium polysulfide 2.5%, items must be submerged in the solution after color developing, wash, dry and wax or varnish colored object ...
Electroless nickel-boron plating developed as a variant of the similar nickel-phosphorus process, discovered accidentally by Charles Adolphe Wurtz in 1844. [2]In 1969, Harold Edward Bellis from DuPont filed a patent for a general class of electroless plating processes using sodium borohydride, dimethylamine borane, or sodium hypophosphite, in the presence of thallium salts, thus producing a ...
Plating is a finishing process in which a metal is deposited on a surface. Plating has been done for hundreds of years; it is also critical for modern technology. Plating is used to decorate objects, for corrosion inhibition, to improve solderability, to harden, to improve wearability, to reduce friction, to improve paint adhesion, to alter conductivity, to improve IR reflectivity, for ...