304 stainless steel is also used in the architectural field for exterior accents such as water and fire features. It is also a common coil material for vaporizers. Early SpaceX Starships used SAE 301 stainless steel in their construction, [ 8 ] before moving over to SAE 304L for the SN7 test tank [ broken anchor ] [ 9 ] and Starship SN8 in 2020.
Stainless steel, due to having a more positive electrode potential than for example carbon steel and aluminium, becomes the cathode, accelerating the corrosion of the anodic metal. An example is the corrosion of aluminium rivets fastening stainless steel sheets in contact with water. [70]
SAE Type 630 stainless steel (more commonly known as 17-4 PH, or simply 17-4; also known as UNS S17400) is a grade of martensitic precipitation hardened stainless steel. It contains approximately 15–17.5% chromium and 3–5% nickel, as well as 3–5% copper. [1] The name comes from the chemical makeup which is approximately 17% chromium and 4 ...
SAE 316L grade stainless steel, sometimes referred to as A4 stainless steel or marine grade stainless steel, is the second most common austenitic stainless steel after 304/A2 stainless steel. Its primary alloying constituents after iron , are chromium (between 16–18%), nickel (10–12%) and molybdenum (2–3%), up to 2% manganese , [ 1 ] with ...
In 200 series stainless steels the structure is obtained by adding manganese and nitrogen, with a small amount of nickel content, making 200 series a cost-effective nickel-chromium austenitic type stainless steel. 300 series stainless steels are the larger subgroup. The most common austenitic stainless steel and most common of all stainless ...
904L is an austenitic stainless steel.It is softer than 316L, [1] [2] and its molybdenum addition gives it superior resistance to localized attack (pitting and crevice corrosion) by chlorides and greater resistance reducing acids; in particular, its copper addition gives it useful corrosion resistance to all concentrations of sulfuric acid.
Ferritic stainless steel alloys are designated as part of the 400-series of stainless steels in the SAE steel grades numbering system. By comparison with austenitic stainless steels, these are less hardenable by cold working and less weldable, but more cost-effective due to the lower nickel content.
Duplex steels also have higher strength. For example, a Type 304 stainless steel has a 0.2% proof strength in the region of 280 MPa (41 ksi), a 22%Cr duplex stainless steel a minimum 0.2% proof strength of some 450 MPa (65 ksi) and a superduplex grade a minimum of 550 MPa (80 ksi). [6]