ISO 18265: "Metallic materials — Conversion of hardness values" (2013) ASTM E140-12B(2019)e1: "Standard Hardness Conversion Tables for Metals Relationship Among Brinell Hardness, Vickers Hardness, Rockwell Hardness, Superficial Hardness, Knoop Hardness, Scleroscope Hardness, and Leeb Hardness" (2019)
The 15T scale employs a 15-kgf load on a 1 ⁄ 16-inch-diameter (1.588 mm) hardened steel ball, and can be used on sheet metal. The B and C scales overlap, such that readings below HRC 20 and those above HRB 100, generally considered unreliable, need not be taken or specified.
Mohs scale of mineral hardness; Mohs hardness of materials (data page) Vickers hardness test; Brinell scale This page was last edited on 16 ...
The typical test uses a 10 mm (0.39 in) diameter steel ball as an indenter with a 3,000 kgf (29.42 kN; 6,614 lbf) force. For softer materials, a smaller force is used; for harder materials, a tungsten carbide ball is substituted for the steel ball. The indentation is measured and hardness calculated as:
Mohs hardness kit, containing one specimen of each mineral on the ten-point hardness scale The Mohs scale ( / m oʊ z / MOHZ ) of mineral hardness is a qualitative ordinal scale , from 1 to 10, characterizing scratch resistance of minerals through the ability of harder material to scratch softer material.
The Vickers hardness test was developed in 1921 by Robert L. Smith and George E. Sandland at Vickers Ltd as an alternative to the Brinell method to measure the hardness of materials. [1] The Vickers test is often easier to use than other hardness tests since the required calculations are independent of the size of the indenter, and the indenter ...
A test takes a mere 2 seconds and, using the standard probe D, leaves an indentation of just ~0.5 mm in diameter on steel or steel casting with a Leeb hardness of 600 HLD. By comparison, a Brinell indentation on the same material is ~3 mm (hardness value ~400 HBW 10/3000), with a standard-compliant measuring time of ~15 seconds plus the time ...
Vickers hardness test (HV), which has one of the widest scales. Widely used to test hardness of all kinds of metal materials (steel, nonferrous metals, tinsel, cemented carbide, sheet metal, etc.); surface layer / coating (Carburization, nitriding, decarburization layer, surface hardening layer, galvanized coating, etc.). [6]