Polyethylene plastic sheet, 4 or 6 thou (0.10 or 0.15 mm), 0.03 US perm (1.7 SI perm). Advanced Polyethylene vapor retarders that pass the ASTM E 1745 standard tests ≤0.3 US perm (17 SI perm). Asphalt-coated kraft paper, often attached to one side of fiberglass batts, 0.40 US perm (22 SI perm). Metallized film
A cross-linked polyethylene (PEX) pipe. Cross-linked polyethylene, commonly abbreviated PEX, XPE or XLPE, is a form of polyethylene with cross-links.It is used predominantly in building services pipework systems, hydronic radiant heating and cooling systems, domestic water piping, insulation for high tension (high voltage) electrical cables, and baby play mats.
Polyethylene absorbs almost no water; the gas and water vapour permeability (only polar gases) is lower than for most plastics. Oxygen, carbon dioxide and flavorings, on the other hand, can pass it easily. Polyethylene burns slowly with a blue flame having a yellow tip and gives off an odour of paraffin (similar to candle flame). The material ...
Polyethylene is a flexible plastic foamed insulation that is widely used to prevent freezing of domestic water supply pipes and to reduce heat loss from domestic heating pipes. The fire performance of Polyethylene is typically 25/50 E84 compliant up to 1" thickness.
HDPE is known for its high strength-to-density ratio. [4] The density of HDPE ranges from 930 to 970 kg/m 3. [5] Although the density of HDPE is only marginally higher than that of low-density polyethylene, HDPE has little branching, giving it stronger intermolecular forces and tensile strength (38 MPa versus 21 MPa) than LDPE. [6]
LLDPE has penetrated almost all traditional markets for polyethylene; it is used for plastic bags and sheets (where it allows using lower thickness than comparable LDPE), plastic wrap, stretch wrap, pouches, toys, covers, lids, pipes, buckets and containers, covering of cables, geomembranes, [2] and mainly flexible tubing. It is also common to ...
A heat-shrinkable sleeve starts out with a thick extruded poly olefin sheet (polyethylene or polypropylene) that is formulated to be cross-linkable. After extruding the thick sheet, it is taken to the "beam" where it is passed under a unit that subjects the sheet to electron irradiation. [2] The irradiation process cross-links the polyolefin.
A common post-extrusion process for plastic sheet stock is thermoforming, where the sheet is heated until soft (plastic), and formed via a mold into a new shape. When vacuum is used, this is often described as vacuum forming. Orientation (i.e. ability/ available density of the sheet to be drawn to the mold which can vary in depths from 1 to 36 ...