It is available in multiple thicknesses and comes in sheets 4 by 8 feet (1.2 by 2.4 m). [ 2 ] [ 3 ] The Homasote Company operates a 750,000-square-foot (70,000 m 2 ) factory in the West Trenton section of Ewing Township, New Jersey .
Masonite board Back side of a masonite board Isorel, c. 1920 Quartrboard, [1] Masonite Corporation, c. 1930. Masonite, also called Quartboard or pressboard, [2] is a type of engineered wood made of steam-cooked and pressure-molded wood or paper fibers. The fibers form a stiff, dense material in a range of weights.
Magnesium oxide wallboard (10 mm thickness) Magnesium oxide, more commonly called magnesia, is a mineral that when used as part of a cement mixture and cast into thin cement panels under proper curing procedures and practices can be used in residential and commercial building construction.
The most common dimension is 1.2 by 2.4 metres (3 ft 11 in × 7 ft 10 in) or the slightly larger imperial dimension of 4 feet × 8 feet. Plies vary in thickness from 1.4 mm to 4.3 mm. The number of plies—which is always odd—depends on the thickness and grade of the sheet. Roofing can use the thinner 16-millimetre (5 ⁄ 8 in) plywood.
A cement board is a combination of cement and reinforcing fibers formed into sheets, of varying thickness that are typically used as a tile backing board. [1] Cement board can be nailed or screwed to wood or steel studs to create a substrate for vertical tile and attached horizontally to plywood for tile floors, kitchen counters and backsplashes.
Board is then cooled, trimmed, sanded and maybe veneered or laminated. UF resins are dominantly used in the MDF industry because of their low cost and fast curing characteristics. [ 2 ] However, pressures on the use of UF resins are mounting steadily due to potential problems associated with formaldehyde emission. [ 3 ]
Particle board, also known as particleboard or chipboard, is an engineered wood product, belonging to the wood-based panels, manufactured from wood chips and a synthetic, mostly formaldehyde based resin or other suitable binder, which is pressed under a hot press, batch- or continuous- type, and produced. [1]
In 1961, at a meeting in Scottsdale, Arizona, the Committee on Grade Simplification and Standardization agreed to what is now the current U.S. standard: in part, the dressed size of a 1-inch (nominal) board was fixed at 3 ⁄ 4 inch; while the dressed size of 2 inch (nominal) lumber was reduced from 1 + 5 ⁄ 8 inch to the current 1 + 1 ⁄ 2 inch.