Mu-metal has several compositions. One such composition is approximately 77% nickel, 16% iron, 5% copper, and 2% chromium or molybdenum. [1] [2]More recently, mu-metal is considered to be ASTM A753 Alloy 4 and is composed of approximately
Strip of permalloy. Permalloy is a nickel–iron magnetic alloy, with about 80% nickel and 20% iron content.Invented in 1914 by physicist Gustav Elmen at Bell Telephone Laboratories, [1] it is notable for its very high magnetic permeability, which makes it useful as a magnetic core material in electrical and electronic equipment, and also in magnetic shielding to block magnetic fields.
Magnetically hard materials have high coercivity, whereas magnetically soft materials have low coercivity. The overall strength of a magnet is measured by its magnetic moment or, alternatively, its total magnetic flux. The local strength of magnetism in a material is measured by its magnetization.
Permeability is typically determined in the lab by application of Darcy's law under steady state conditions or, more generally, by application of various solutions to the diffusion equation for unsteady flow conditions. [8] Permeability needs to be measured, either directly (using Darcy's law), or through estimation using empirically derived ...
Permendur rods. Permendur is a cobalt-iron soft ferromagnetic alloy with equal parts of cobalt and iron which is notable for its high magnetic saturation level. [1] [2] Its saturation flux density of around 2.4 tesla is the highest of any commercially available metal.
Different materials have different saturation levels. For example, high permeability iron alloys used in transformers reach magnetic saturation at 1.6–2.2 teslas (T), [4] whereas ferrites saturate at 0.2–0.5 T. [5] Some amorphous alloys saturate at 1.2–1.3 T. [6] Mu-metal saturates at around 0.8 T. [7] [8]
Permeability is influenced by the spacing between the grains, which form distributed air gap; the less gap, the higher permeability and the less-soft saturation. Due to large difference of densities, even a small amount of binder, weight-wise, can significantly increase the volume and therefore intergrain spacing.
They also have high magnetic permeability. These so-called ceramic magnets are cheap, and are widely used in household products such as refrigerator magnets . The maximum magnetic field B is about 0.35 tesla and the magnetic field strength H is about 30–160 kiloampere turns per meter (400–2000 oersteds ). [ 33 ]