Tensile testing, also known as tension testing, [1] is a fundamental materials science and engineering test in which a sample is subjected to a controlled tension until failure. Properties that are directly measured via a tensile test are ultimate tensile strength, breaking strength, maximum elongation and reduction in area. [2]
The ultimate tensile strength of a material is an intensive property; therefore its value does not depend on the size of the test specimen.However, depending on the material, it may be dependent on other factors, such as the preparation of the specimen, the presence or otherwise of surface defects, and the temperature of the test environment and material.
The ultimate strength is the maximum stress that a material can withstand before it breaks or weakens. [12] For example, the ultimate tensile strength (UTS) of AISI 1018 Steel is 440 MPa. In Imperial units, the unit of stress is given as lbf/in 2 or pounds-force per square inch. This unit is often abbreviated as psi.
ASTM A992 steel is a structural steel alloy often used in the US for steel wide-flange and I beams. Like other carbon steels, the density of ASTM A992 steel is approximately 7850 kg/m 3 (0.2836 lb/in 3).
Brookhaven National Laboratory (through Brookhaven Science Associates, LLC – a collaboration between Battelle and Stony Brook University) Idaho National Laboratory (through the Battelle Energy Alliance – a collaboration between Battelle, BWX Technologies, Inc., Washington Group International, Electric Power Research Institute and an ...
Entering Week 16 of the 2024 season, the Las Vegas Raiders have the first overall pick in the 2025 NFL draft.They're one of two 2-12 teams, along with the Giants, but are favored this week against ...
The factor of safety on ultimate tensile strength is to prevent sudden fracture and collapse, which would result in greater economic loss and possible loss of life. An aircraft wing might be designed with a factor of safety of 1.25 on the yield strength of the wing and a factor of safety of 1.5 on its ultimate strength.