Hard chrome plating. Hard chrome, also known as industrial chrome or engineered chrome, is used to reduce friction, improve durability through abrasion tolerance and wear resistance in general, minimize galling or seizing of parts, expand chemical inertness to include a broader set of conditions (such as oxidation resistance), and bulking ...
For aluminum, the chromate conversion bath can be simply a solution of chromic acid. The process is rapid (1–5 min), requires a single ambient temperature process tank and associated rinse, and is relatively trouble free. [2] As of 1995, Henkel's Alodine 1200s commercial formula for aluminum consisted of 50-60% chromic anhydride CrO
A #7 finish is produced by polishing with a 280–320 grit belt or wheel and sisal buffing with a cut and color compound. This is a semi-bright finish that will still have some polishing lines but they will be very dull. Carbon steel and iron are commonly polished to a #7 finish before chrome plating.
Black nickel plating was developed around 1905, and between the two wars, black chrome plating (first German patent 1929.GP 607, 420), which saw wider use only from the mid-1950s. [14] After the First World War, the first procedures for anodic oxidation and coloring of anodically oxidized aluminium were developed (1923, 1924.DRP. 413876).
Frenching is the act of recessing or moulding a headlight, taillight, antenna or number plate into a car body to give a smoother look to the vehicle. The name originates from the end result looking like a French cuff of a shirt sleeve, which has a ridge at the end.
Polishing is often used to enhance the appearance of an item, prevent contamination of instruments, remove oxidation, create a reflective surface, or prevent corrosion in pipes. In metallography and metallurgy, polishing is used to create a flat, defect-free surface for examination of a metal's microstructure under a microscope. Silicon-based ...
Get AOL Mail for FREE! Manage your email like never before with travel, photo & document views. Personalize your inbox with themes & tabs. You've Got Mail!
4. Acid chrome plating is dependent on a "slime layer" containing Cr(+2) that is critical, formed in the initial start of current. 5. Cr(+3) plating isn't new or difficult and has much better throwing power and adhesion to base metals. Problem is matte finish. Great for corrosion resistant plate of small parts but more common zinc-nickel etc ...