The specific cooling rate that is necessary to avoid the formation of pearlite is a product of the chemistry of the austenite phase and thus the alloy being processed. The actual cooling rate is a product of both the quench severity, which is influenced by quench media, agitation, load (quenchant ratio, etc.), and the thickness and geometry of ...
A cooling curve of naphthalene from liquid to solid. A cooling curve is a line graph that represents the change of phase of matter, typically from a gas to a solid or a liquid to a solid. The independent variable (X-axis) is time and the dependent variable (Y-axis) is temperature. [1] Below is an example of a cooling curve used in castings.
However, greater undercooling by rapid quenching results in formation of martensite or bainite instead of pearlite. This is possible provided the cooling rate is such that the cooling curve intersects the martensite start temperature or the bainite start curve before intersecting the P s curve. The martensite transformation being a ...
There are two types of continuous cooling diagrams drawn for practical purposes. Type 1: This is the plot beginning with the transformation start point, cooling with a specific transformation fraction and ending with a transformation finish temperature for all products against transformation time for each cooling curve.
English: The cooling curve and phase diagram of an alloy; in this case a copper/nickel alloy. Based on a diagram from Degarmo, E. Paul; Black, J T.; Kohser, Ronald A. (2003), Materials and Processes in Manufacturing (9th ed.), Wiley, ISBN 0-471-65653-4 .
English: Example of a cooling curve of a pure metal or eutectic alloy, with various aspects pointed out. Based on image from Degarmo, E. Paul; Black, J T.; Kohser, Ronald A. (2003), Materials and Processes in Manufacturing (9th ed.), Wiley, ISBN 0-471-65653-4.
The cooling rate will be highest at the end being quenched, and will decrease as distance from the end increases. Subsequent to cooling a flat surface is ground on the test piece and the hardenability is then found by measuring the hardness along the bar. The farther away from the quenched end that the hardness extends, the higher the ...
Eutectic alloys have two or more materials and have a eutectic composition. When a non-eutectic alloy solidifies, its components solidify at different temperatures, exhibiting a plastic melting range. Conversely, when a well-mixed, eutectic alloy melts, it does so at a single, sharp temperature.