Tempering is a process of heat treating, which is used to increase the toughness of iron-based alloys. Tempering is usually performed after hardening, to reduce some of the excess hardness, and is done by heating the metal to some temperature below the critical point for a certain period of time, then allowing it to cool in still air. The exact ...
A cold work steel used for gauges, cutting tools, woodworking tools and knives. It can be hardened to 66 HRC, typically used at 61-63 HRC. Also sold as 1.2842 and 90MnCrV8. [9] O6: 1.45% C, 1.0% Mn, 1.0% Si, 0.3% Mo: A cold work graphitic steel with outstanding resistance to metal-to-metal sliding wear and galling.
Holloman and Jaffe determined the value of C experimentally by plotting hardness versus tempering time for a series of tempering temperatures of interest and interpolating the data to obtain the time necessary to yield a number of different hardness values. This work was based on six different heats of plain carbon steels with carbon contents ...
To examine a piece of steel, obtain a hand file and file an edge of the selected metal. If the piece of steel has not undergone the hardening process, the metal file should easily 'bite' into the sample. If the metal has been hardened, the file fails to cut into the sample and glances off with little visible effect.
Differential tempering begins by taking steel that has been uniformly quenched and hardened, and then heating it in localized areas to reduce the hardness. The process is often used in blacksmithing for tempering cutting instruments, softening the back, shaft, or spine, but simultaneously tempering the edge to a very high hardness. The process ...
Stainless steel is a popular class of material for knife blades because it resists corrosion and is easy to maintain. However, it is not impervious to corrosion or rust. For a steel to be considered stainless it must have a Chromium content of at least 10.5%. [24] 154CM / ATS-34 steels. These two steels are practically identical in composition ...
300 series stainless steels are the larger subgroup. The most common austenitic stainless steel and most common of all stainless steel is Type 304, also known as 18/8 or A2. Type 304 is extensively used in such items as cookware, cutlery, and kitchen equipment. Type 316, also known as A4, is the next most common austenitic stainless steel.
High-speed steel (HSS or HS) is a subset of tool steels, commonly used as cutting tool material. It is superior to high-carbon steel tools in that it can withstand higher temperatures without losing its temper (hardness). This property allows HSS to cut faster than high carbon steel, hence the name high-speed steel.