Dyneema Composite Fabric (DCF) is a laminated material consisting of a grid of Dyneema threads sandwiched between two thin transparent polyester membranes. This material is very strong for its weight, and was originally developed for use in racing yacht sails under the name 'Cuben Fiber'.
M5 has a tensile strength of 4 GPa [1] to 9.5GPa. [2] Other aramids- (such as Kevlar and Twaron) or UHMWPE-fibres (such as Dyneema and Spectra) range from 2.2 to 3.9 GPa. [3]M5 has "very high levels" of fire resistance, flame retardancy, and chemical resistance, especially high for an organic fiber.
Dyneema Composite Fabric (DCF), also known as Cuben Fiber (CTF3), is a high-performance non-woven composite material used in high-strength, low-weight applications. It is constructed from a thin sheet of ultra-high-molecular-weight polyethylene ( UHMWPE , "Dyneema") laminated between two sheets of polyester .
Kevlar (para-aramid) [2] is a strong, heat-resistant synthetic fiber, related to other aramids such as Nomex and Technora.Developed by Stephanie Kwolek at DuPont in 1965, [3] [2] [4] the high-strength material was first used commercially in the early 1970s as a replacement for steel in racing tires.
Dyneema, a braided Ultra High Molecular Weight Polyethylene (UHMWPE) line, and the identically structured line, Spectra, are stronger and lighter than Kevlar for a given diameter. One of the most important characteristics of line for high altitude kite flying is small diameter and high strength to weight ratio.
Webbing is less likely to loosen itself off the rock than tubular rope. Note that webbing construction is either utterly flat or flat-tubular; the latter tends to handle better but knots are more likely to jam. The most popular knots in webbing are the water knot and the grapevine knot. The latter is stronger, but uses more webbing for the knot.
Zylon body armor panels sometimes cost twice as much as Kevlar or 35% more than other advanced materials. [9] Despite "sticker shock", the marketing for Zylon body armor described incredibly low weight and thickness, but shockingly high protection, causing some to refer to it as a "miracle fiber".
Structure of Twaron and Kevlar.The aromatic rings appear as hexagons. The rings are attached alternately to either two NH groups or two CO groups. The attachment points on each ring are diametrically opposite each other, a characteristic of the structure called para-aramid.