Tempered or toughened glass is a type of safety glass processed by controlled thermal or chemical treatments to increase its strength compared with normal glass. Tempering puts the outer surfaces into compression and the interior into tension .
Unless stated otherwise, the properties of fused silica (quartz glass) and germania glass are derived from the SciGlass glass database by forming the arithmetic mean of all the experimental values from different authors (in general more than 10 independent sources for quartz glass and T g of germanium oxide glass). The list is not exhaustive.
Toughened glass is processed by controlled thermal or chemical treatments to increase its strength compared with normal glass. [6] Tempering, by design, creates balanced internal stresses which causes the glass sheet, when broken, to crumble into small granular chunks of similar size and shape instead of splintering into random, jagged shards.
Also unlike toughened glass, chemically strengthened glass may be cut after strengthening, but loses its added strength within approximately 20 mm of the cut. Similarly, when the surface of chemically strengthened glass is deeply scratched, this area loses its additional strength. Another negative of chemically strengthened glass is the added cost.
In automobiles, the laminated glass panel is around 6.5 mm (0.26 inches) thick, in comparison to airplane glass being three times as thick. [21] In airliners on the front and side cockpit windows, there is often three plies of 4 mm toughened glass with 2.6 mm thick PVB between them.
A glass building facade. Glass is an amorphous (non-crystalline) solid.Because it is often transparent and chemically inert, glass has found widespread practical, technological, and decorative use in window panes, tableware, and optics.
Glass fibers have a much higher tensile strength than regular glass (200-500 times stronger than regular glass). [7] This is due to the reduction of flaws in glass fibers [8] and the small cross sectional area of glass fibers, constraining maximum defect size.
The first principle is used in laminated glass where two sheets of glass are separated by an interlayer of polyvinyl butyral. The polyvinyl butyral, as a viscoelastic polymer, absorbs the growing crack. The second method is used in toughened glass and pre-stressed concrete. A demonstration of glass toughening is provided by Prince Rupert's Drop.