Polyether ether ketone (PEEK) is a colourless organic thermoplastic polymer in the polyaryletherketone (PAEK) family, used in engineering applications. It was invented in November 1978 [2] and brought to market in the early 1980s by part of Imperial Chemical Industries (ICI), the PEEK division was acquired through a management buyout, giving rise to Victrex PLC.
It also affects its heat resistance and processing temperature. The higher the ratio of ketones the more rigid the polymer chain, which results in a higher glass transition temperature and melting point. The processing temperatures can range from 350 to 430 °C. [1] [3] [4] Plastics that fall within this family include: [3] PEK; PEEK; PEKK; PEEKK
Polyetherketones (PEK for short) are polymers whose molecular backbone contain alternating ketone (R-CO-R) and Ether (R-O-R) functionalities. The most common are Polyaryletherketones (PAEK), in which there is an aryl group linked in the (1–4)-position between each of the functional groups.
Polyetherimide (PEI; branded as Ultem [1]) is an amorphous, amber-to-transparent thermoplastic with characteristics similar to the related plastic PEEK.When comparing PEI to PEEK, the former is cheaper but has lower impact strength and a tighter temperature range.
Vespel is used in high-resolution probes for NMR spectroscopy because its volume magnetic susceptibility (−9.02 ± 0.25×10 −6 for Vespel SP-1 at 21.8 °C [5]) is close to that of water at room temperature (−9.03×10 −6 at 20 °C [6]) Negative values indicate that both substances are diamagnetic.
Poly(p-phenylene oxide) (PPO), poly(p-phenylene ether) (PPE), poly(oxy-2,6-dimethyl-1,4-phenylene), often referred to simply as polyphenylene oxide, is a high-temperature thermoplastic with the general formula (C 8 H 8 O) n. It is rarely used in its pure form due to difficulties in processing.
The heat deflection temperature or heat distortion temperature (HDT, HDTUL, or DTUL) is the temperature at which a polymer or plastic sample deforms under a specified load. [1] This property of a given plastic material is applied in many aspects of product design, engineering and manufacture of products using thermoplastic components.
Vicat softening temperature or Vicat hardness is the determination of the softening point for materials that have no definite melting point, such as plastics. It is taken as the temperature at which the specimen is penetrated to a depth of 1 mm by a flat-ended needle with a 1 mm 2 circular or square cross-section.