The main effect of chloride ions on reinforced concrete is to cause pitting corrosion of the steel reinforcement bars (rebar). It is a surreptitious and dangerous form of localized corrosion because the rebar sections can be decreased to the point that the steel reinforcement are no longer capable to withstand to the tensile efforts they are ...
Over time, the thin film can be damaged, and corrosion of steel rebar starts. The corrosion of steel rebar is one of the main causes of premature failure of reinforced concrete structures worldwide, [4] mainly as a consequence of two degradation processes, carbonation and penetration of chlorides. [1]
Corrosion is a natural process that converts a refined metal into a more chemically stable ... It is one of the most common failure modes of reinforced concrete ...
Oxide jacking has caused concrete spalling on walls of the Herbst Pavilion at Fort Mason Center in San Francisco. The expansive force of rusting, which may be called oxide jacking or rust burst, is a phenomenon that can cause damage to structures made of stone, masonry, concrete or ceramics, and reinforced with metal components.
In wet and cold climates, reinforced concrete for roads, bridges, parking structures and other structures that may be exposed to deicing salt may benefit from use of corrosion-resistant reinforcement such as uncoated, low carbon/chromium (micro composite), epoxy-coated, hot dip galvanized or stainless steel rebar. Good design and a well-chosen ...
Daily, Steven F, Using Cathodic Protection to Control Corrosion of Reinforced Concrete Structures in Marine Environments (published in Port Technology International) Gummow, RA, Corrosion Control of Municipal Infrastructure Using Cathodic Protection. NACE Conference Oct 1999, NACE Materials Performance Feb 2000
Get AOL Mail for FREE! Manage your email like never before with travel, photo & document views. Personalize your inbox with themes & tabs. You've Got Mail!
Pitting corrosion, or pitting, is a form of extremely localized corrosion that leads to the random creation of small holes in metal. The driving power for pitting corrosion is the depassivation of a small area, which becomes anodic (oxidation reaction) while an unknown but potentially vast area becomes cathodic (reduction reaction), leading to ...