Brittle fracture in glass Fracture of an aluminum crank arm of a bicycle, where the bright areas display a brittle fracture, and the dark areas show fatigue fracture. In brittle fracture, no apparent plastic deformation takes place before fracture. Brittle fracture typically involves little energy absorption and occurs at high speeds—up to ...
Brittle fracture in glass Brittle fracture in cast iron tensile testpieces. A material is brittle if, when subjected to stress, it fractures with little elastic deformation and without significant plastic deformation. Brittle materials absorb relatively little energy prior to fracture, even those of high strength. Breaking is often accompanied ...
Concrete fracture analysis is part of fracture mechanics that studies crack propagation and related failure modes in concrete. [17] As it is widely used in construction, fracture analysis and modes of reinforcement are an important part of the study of concrete, and different concretes are characterized in part by their fracture properties. [ 18 ]
fracture front – the line separating the rock that has been fractured from the rock that has not; fracture tip – the point at which the fracture trace terminates on the surface; fracture trace – the line representing the intersection of the fracture plane with the surface; Griffith cracks – preexisting microfractures and flaws in the rock
Linear elastic fracture mechanics predicts that a crack will extend when the stress intensity factor at the crack tip is greater than the fracture toughness of the material. Therefore, the critical applied stress can also be determined once the stress intensity factor at a crack tip is known.
Embrittlement is used to describe any phenomena where the environment compromises a stressed material's mechanical performance, such as temperature or environmental composition. This is oftentimes undesirable as brittle fracture occurs quicker and can much more easily propagate than ductile fracture, leading to complete failure of the equipment.
Moreover, some (brittle) materials fracture before the onset of necking, such that there is no peak. In practice, for many purposes it is preferable to carry out a different kind of test, designed to evaluate the toughness (energy absorbed during fracture), rather than use ductility values obtained in tensile tests.
In fracture mechanics, the stress intensity factor (K) is used to predict the stress state ("stress intensity") near the tip of a crack or notch caused by a remote load or residual stresses. [1] It is a theoretical construct usually applied to a homogeneous, linear elastic material and is useful for providing a failure criterion for brittle ...