One reason for this type of defect is excessive current, which causes the edges of the joint to melt and drain into the weld, thus leaving a drain-like impression along the length of the weld. Another reason is poor technique that doesn't deposit enough filler metal along the edges of the weld.
In welding, undercutting is when the weld reduces the cross-sectional thickness of the base metal. This type of defect reduces the strength of the weld and workpieces. One reason for this defect is excessive current, causing the edges of the joint to melt and drain into the weld; this leaves a drain-like impression along the length of the weld.
Arc blow tends to occur if the material being welded has residual magnetism at a certain level, particularly when the weld root is being made, and the welding current is direct current (DC positive or negative). Magnetic arc blow is popularly attributed to a change in the direction of current as it flows into and through the workpiece.
During welding, joints are formed between two or more separate pieces of material which can introduce defects or residual stresses. Under cyclic loading these defects can grow a fatigue crack, causing the assembly to fail even if these cyclic stresses are low and smaller than the base material and weld filler material yield stress. [1]
Engineering Critical Assessment (ECA) is a procedure by which the safety of a welded structure with defects or flaws can be determined. ECAs utilize the material properties and expected stress history to determine a flaw acceptance criteria which will ensure that welds will not fail during the construction or service life of the welded structure. [1]
In manufacturing, the Weld line or Knit line or Meld line is the line where two flow fronts meet when there is the inability of two or more flow fronts to "knit" together, or "weld", during the molding process. These lines usually occur around holes or obstructions and cause locally weak areas in the molded part. [1]
Get AOL Mail for FREE! Manage your email like never before with travel, photo & document views. Personalize your inbox with themes & tabs. You've Got Mail!
Amongst these, tunneling defect is the most common defect in DFSW resulting from improper material flows throughout welding. It is mainly attributed to inappropriate selection of welding parameters particularly welding speed, rotational speed, tool design and tool penetration leading to either abnormal stirring or insufficient heat input. [18]