Cold cracking—also known as delayed cracking, hydrogen-assisted cracking (HAC), or hydrogen-induced cracking (HIC)—is a type of defect that often develops after solidification of the weld when the temperature starts to drop from about 190 °C (375 °F); the phenomenon often arises at room temperature, and it can take up to 24 hours to appear even after complete cooling. [8]
Engineering Critical Assessment (ECA) is a procedure by which the safety of a welded structure with defects or flaws can be determined. ECAs utilize the material properties and expected stress history to determine a flaw acceptance criteria which will ensure that welds will not fail during the construction or service life of the welded structure. [1]
Weld defects such as misalignment, porosity, lack of fusion and degradation of the matrix and/or fibers may be visually apparent. Subsurface defects may not be visible, unless the composite matrix was nearly transparent and the embedded fibers did not obscure them. [6] Ultrasonic A-scan display showing a reflector in the part being tested.
Weld mapping is the process of assigning information to a weld repair or joint to enable easy identification of weld processes, production (welders, their qualifications, date welded), quality (visual inspection, NDT, standards and specifications) and traceability (tracking weld joints and welded castings, the origin of weld materials).
In welding, undercutting is when the weld reduces the cross-sectional thickness of the base metal. This type of defect reduces the strength of the weld and workpieces. One reason for this defect is excessive current, causing the edges of the joint to melt and drain into the weld; this leaves a drain-like impression along the length of the weld.
During the welding process, residual stresses can present themselves in the area of the weld, either in the heat affected zone or fusion zone. The mean stress a welded joint may see in application, can be altered due to the welding processes implementing residual stresses, changing the fatigue life and can render S-N laboratory testing results. [2]
800 A-scans were used to create a 2D image and 1000 images were put together to make the final 3D image. By looking at the border region between the perfect and imperfect weld, they were able to evaluate the effectiveness of OCT in finding weld defects. Air bubbles were visually apparent in the imperfectly welded region.
Welding slag is a form of slag, or vitreous material produced as a byproduct of some arc welding processes, most specifically shielded metal arc welding (also known as stick welding), submerged arc welding, and flux-cored arc welding.