Dyneema composite fabric (DCF) is a laminated material consisting of a grid of Dyneema threads sandwiched between two thin transparent polyester membranes. This material is very strong for its weight, and was originally developed for use in racing yacht sails under the name 'Cuben Fiber'.
DuPont made public in 1938 that their company had invented nylon. [1] This new invention was the first synthetic fiber, fabrics that are commonly used in textiles today. [2] In 1939, DuPont began marketing nylon monofilament fishing lines; however, braided Dacron lines remained the most used and popular fishing line for the next two decades, as early monofilament line was very stiff or "wiry ...
Dyneema Composite Fabric (DCF), also known as Cuben Fiber (CTF3), is a high-performance non-woven composite material used in high-strength, low-weight applications. It is constructed from a thin sheet of ultra-high-molecular-weight polyethylene ( UHMWPE , "Dyneema") laminated between two sheets of polyester .
Kevlar (para-aramid) [2] is a strong, heat-resistant synthetic fiber, related to other aramids such as Nomex and Technora.Developed by Stephanie Kwolek at DuPont in 1965, [3] [2] [4] the high-strength material was first used commercially in the early 1970s as a replacement for steel in racing tires.
Braided lines often have 1/3 to 1/4 the diameter of mono or fluorocarbon lines at a given test breaking strength. Therefore, it is easy to fit much longer braided line on a spool than monofilament or fluorocarbon line for the same strength. This is very important for deep sea fishing, since reels don't have to be very big to accommodate long lines.
A 240 centimetres (94 in) Sling A climbing anchor equalized using dyneema slings. 1957 article on use of slings by Jan and Herb Conn.. A sling is an item of climbing equipment consisting of a tied or sewn loop of webbing.
The specific strength is bounded to be no greater than c 2 ≈ 9 × 10 13 kN⋅m/kg, where c is the speed of light. This limit is achieved by electric and magnetic field lines, QCD flux tubes, and the fundamental strings hypothesized by string theory. [citation needed]
Bulk moduli, shear moduli, and elasticity are the key factors in the superhard classification process. The incompressibility of a material is quantified by the bulk modulus B, which measures the resistance of a solid to volume compression under hydrostatic stress as B = −Vdp/dV.