Polybenzimidazole (PBI, short for poly[2,2’-(m-phenylen)-5,5’-bisbenzimidazole]) fiber is a synthetic fiber with a very high decomposition temperature. It does not exhibit a melting point, it has exceptional thermal and chemical stability, and it does not readily ignite. [1]
Polyvinyl alcohol (PVOH, PVA, or PVAl) is a water-soluble synthetic polymer. It has the idealized formula [CH 2 CH(OH)] n. It is used in papermaking, textile warp sizing, as a thickener and emulsion stabilizer in polyvinyl acetate (PVAc) adhesive formulations, in a variety of coatings, and 3D printing. It is colourless (white) and odorless.
Liquid crystallinity in polymers may occur either by dissolving a polymer in a solvent (lyotropic liquid-crystal polymers) or by heating a polymer above its glass or melting transition point (thermotropic liquid-crystal polymers). [6] Liquid-crystal polymers are present in melted/liquid or solid form. [7]
Linear polyethyleneimine is soluble in hot water, at low pH, in methanol, ethanol, or chloroform. It is insoluble in cold water, benzene, ethyl ether, and acetone. Linear polyethylenimine has a melting point of around 67 °C. [3] Both linear and branched polyethylneimine can be stored at room temperature.
Polyacrylate emulsion, water-borne coating, are used as binder for outdoor and indoor "latex" house paints.; Acrylic paints as artist paints.; Acrylic fibre.; Sodium polyacrylate water-soluble thickeners, a polymer for the production of the Superabsorbent polymer (SAP) used in disposable diapers due to its high absorbency per unit mass.
It was made into the spun fiber at DuPont in 1942 and marketed under the name of Orlon. Acrylonitrile is commonly employed as a comonomer with styrene, e.g. acrylonitrile, styrene and acrylate plastics. Labelling of items of clothing with acrylic (see acrylic fiber) means the polymer consists of at least 85% acrylonitrile as the monomer. A ...
Soluble in chloroform and other chlorinated hydrocarbons. [10] Biocompatible and hence is suitable for medical applications. Melting point 175 °C., and glass transition temperature 2 °C. Tensile strength 40 MPa, close to that of polypropylene. Sinks in water (while polypropylene floats), facilitating its anaerobic biodegradation in sediments.
Perfectly isotactic PP has a melting point of 171 °C (340 °F). Commercial isotactic PP has a melting point that ranges from 160 to 166 °C (320 to 331 °F), depending on atactic material and crystallinity. Syndiotactic PP with a crystallinity of 30% has a melting point of 130 °C (266 °F). [8] Below 0 °C, PP becomes brittle. [9]