Aluminium anodizing (eloxal or Electrolytic Oxidation of Aluminium) [12] is usually performed in an acidic solution, typically sulphuric acid or chromic acid, which slowly dissolves the aluminium oxide. The acid action is balanced with the oxidation rate to form a coating with nanopores, 10–150 nm in diameter. [6]
For aluminum, the chromate conversion bath can be simply a solution of chromic acid. The process is rapid (1–5 min), requires a single ambient temperature process tank and associated rinse, and is relatively trouble free. [2] As of 1995, Henkel's Alodine 1200s commercial formula for aluminum consisted of 50-60% chromic anhydride CrO
A conversion coating is a chemical or electro-chemical treatment applied to manufactured parts that superficially converts the material into a thin adhering coating of an insoluble compound.
This kind of chromic acid may be used as a cleaning mixture for glass. Chromic acid may also refer to the molecular species, H 2 CrO 4 of which the trioxide is the anhydride. Chromic acid features chromium in an oxidation state of +6 (and a valence of VI or 6). It is a strong and corrosive oxidizing agent and a moderate carcinogen.
Chrome alum or Chromium(III) potassium sulfate is the potassium double sulfate of chromium. Its chemical formula is KCr(SO 4 ) 2 and it is commonly found in its dodecahydrate form as KCr(SO 4 ) 2 ·12(H 2 O).
Chromium(III) sulfate are commonly obtained from the wastes of chromate oxidations of various organic compounds. Anthraquinone and quinone are produced on large scale by the x treatment of respectively anthracene and phenol with chromic acid. A chromium(III) oxide byproduct is generated, which is readily extracted into sulfuric acid.
Black for aluminum. Boil a solution of 20 g ammonium molybdate and 5 g of sodium thiosulfate in a liter of water, immerse the objects, rinse, dry, wax or lacquer after the development of color. [31] Lustre colours. Use a solution of 280 g of sodium thiosulphate, 25 g of cupric acetate and 30 g of citric acid. It can be used on copper and its ...
Anodic aluminum oxide, anodic aluminum oxide (AAO), or anodic alumina is a self-organized form of aluminum oxide that has a honeycomb-like structure formed by high density arrays of uniform and parallel pores. The diameter of the pores can be as low as 5 nanometers and as high as several hundred nanometers, and length can be controlled from few ...