Galvanic corrosion of an aluminium plate occurred when the plate was connected to a mild steel structural support.. Galvanic corrosion occurs when two different metals have physical or electrical contact with each other and are immersed in a common electrolyte, or when the same metal is exposed to electrolyte with different concentrations.
Using the same metal for all construction is the easiest way of matching potentials. Electroplating or other plating can also help. This tends to use more noble metals that resist corrosion better. Chrome, nickel, silver and gold can all be used. Galvanizing with zinc protects the steel base metal by sacrificial anodic action.
Erosion corrosion is a form of corrosion damage usually on a metal surface caused by turbulence of a liquid or solid containing liquid and the metal surface. [67] Aluminum can be particularly susceptible due to the fact that the aluminum oxide layer which affords corrosion protection to the underlying metal is eroded away. [68] [69]
Stress corrosion cracking (SCC) is the growth of crack formation in a corrosive environment. It can lead to unexpected and sudden failure of normally ductile metal alloys subjected to a tensile stress, especially at elevated temperature.
Pitting corrosion, or pitting, is a form of extremely localized corrosion that leads to the random creation of small holes in metal. The driving power for pitting corrosion is the depassivation of a small area, which becomes anodic (oxidation reaction) while an unknown but potentially vast area becomes cathodic (reduction reaction), leading to ...
The galvanic series (or electropotential series) determines the nobility of metals and semi-metals. When two metals are submerged in an electrolyte, while also electrically connected by some external conductor, the less noble (base) will experience galvanic corrosion. The rate of corrosion is determined by the electrolyte, the difference in ...
In true corrosion fatigue, the fatigue-crack-growth rate is enhanced by corrosion; this effect is seen in all three regions of the fatigue-crack growth-rate diagram. The diagram on the left is a schematic of crack-growth rate under true corrosion fatigue; the curve shifts to a lower stress-intensity-factor range in the corrosive environment.
In general, crevice corrosion is of greatest concern for materials which are normally passive metals, like stainless steel or aluminum. Crevice corrosion tends to be of greatest significance to components built of highly corrosion-resistant superalloys and operating with the purest-available water chemistry.