2. Solderability - Wikipedia

   en.wikipedia.org/wiki/Solderability

   Solders have to be specially selected to avoid galvanic corrosion problems. Tin-zinc solders have proven to be reliable in joining aluminum to aluminum and aluminum to copper. [3] They most often require flux and brushing with a stainless steel brush to break oxide coating to achieve proper bond. Difficult: High alloy steel Stainless steels

3. Solder alloys - Wikipedia

   en.wikipedia.org/wiki/Solder_alloys

   Used for soldering iron and steel [28] Pb 54 Sn 45 Ag 1: 177: 210: Pb: exceptional strength, silver gives it a bright long-lasting finish; ideal for stainless steel [54] Sn 56 Pb 39 Ag 5: Pb [55] Sn 62.5 Pb 36 Ag 2.5: 179 [11] Pb: Yes: Sn 62 Pb 36 Ag 2: 179 [11] Pb: Yes: Sn62. Common in electronics. The strongest tin-lead solder. Appearance ...

4. Soldering - Wikipedia

   en.wikipedia.org/wiki/Soldering

   Soldering (US: / ˈ s ɒ d ər ɪ ŋ /; UK: / ˈ s oʊ l d ər ɪ ŋ /) is a process of joining two metal surfaces together using a filler metal called solder. The soldering process involves heating the surfaces to be joined and melting the solder, which is then allowed to cool and solidify, creating a strong and durable joint.

5. Flux (metallurgy) - Wikipedia

   en.wikipedia.org/wiki/Flux_(metallurgy)

   Stainless steel is a material which is difficult to solder because of its stable, self-healing surface oxide layer and its low thermal conductivity. A solution of zinc chloride in hydrochloric acid is a common flux for stainless steels; it has however to be thoroughly removed afterwards as it would cause pitting corrosion .

6. List of brazing alloys - Wikipedia

   en.wikipedia.org/wiki/List_of_brazing_alloys

   Similar to BAg-1, more economical. For ferrous, nonferrous and dissimilar alloys. Free-flowing, for larger gaps, where fillets are desired. For steel, stainless steel, copper, copper alloys, nickel, nickel alloys, and combinations. Light yellow color. Maximum service temperature 204 °C, intermittently 316 °C. 26: 21: 35: 18: Ag 30 Cu 28 Zn 21 ...

7. Solder - Wikipedia

   en.wikipedia.org/wiki/Solder

   Solder (UK: / ˈ s ɒ l d ə, ˈ s ə ʊ l d ə /; [1] NA: / ˈ s ɒ d ər /) [2] is a fusible metal alloy used to create a permanent bond between metal workpieces. Solder is melted in order to wet the parts of the joint, where it adheres to and connects the pieces after cooling.