Machinability is the ease with which a metal can be cut permitting the removal of the material with a satisfactory finish at low cost. [1] Materials with good machinability (free machining materials) require little power to cut, can be cut quickly, easily obtain a good finish, and do not cause significant wear on the tooling.
Monel alloy 405, also known as Monel R405, is the free-machining grade of alloy 400. [26] The nickel, carbon, manganese, iron, silicon & copper percent remains the same as alloy 400, but the sulfur is increased from 0.024 max to 0.025-0.060%. Alloy 405 is used chiefly for automatic screw machine stock and is not generally recommended for other ...
Waspaloy is an age-hardenable, nickel-based superalloy with excellent strength properties through temperatures of roughly 980°C (1800°F). Other characteristics of Waspaloy include good corrosion resistance, as well as being relatively impervious to oxidation making it well suited for service in extreme environments.
Inconel alloys are oxidation- and corrosion-resistant. When heated, Inconel forms a thick, stable, passivating oxide layer protecting the surface from further attack. Inconel retains strength over a wide temperature range, attractive for high-temperature applications where aluminum and steel would succumb to creep as a result of thermally ...
Nickel titanium, also known as nitinol, is a metal alloy of nickel and titanium, where the two elements are present in roughly equal atomic percentages. Different alloys are named according to the weight percentage of nickel; e.g., nitinol 55 and nitinol 60 .
Strip of permalloy. Permalloy is a nickel–iron magnetic alloy, with about 80% nickel and 20% iron content.Invented in 1914 by physicist Gustav Elmen at Bell Telephone Laboratories, [1] it is notable for its very high magnetic permeability, which makes it useful as a magnetic core material in electrical and electronic equipment, and also in magnetic shielding to block magnetic fields.
Originally developed to produce oxide-dispersion strengthened (ODS) nickel- and iron-base superalloys for applications in the aerospace industry, [1] MA has now been shown to be capable of synthesizing a variety of equilibrium and non-equilibrium alloy phases starting from blended elemental or pre-alloyed powders. [2]
Like other nickel/iron compositions, Invar is a solid solution; that is, it is a single-phase alloy.In one commercial grade called Invar 36 it consists of approximately 36% nickel and 64% iron, [4] has a melting point of 1427C, a density of 8.05 g/cm3 and a resistivity of 8.2 x 10-5 Ω·cm. [5] The invar range was described by Westinghouse scientists in 1961 as "30–45 atom per cent nickel".