Shrinkage and Contraction can again be classified into liquid shrinkage and solid contraction. Liquid shrinkage is the reduction in volume during the process of solidification (liquid to solid), the liquid shrinkage is accounted for by risers. Solid contraction is the reduction in dimensions during the cooling of the (solid) cast metal.
Heat-setting of synthetic fabrics eliminates the internal tensions within the fiber, generated during manufacturing, and the new state can be fixed by rapid cooling. This heat setting fixes the fabrics in the relaxed state, and thus avoids subsequent shrinkage or creasing of the fabric.
Silk surfacing a surface finishing of cotton to obtain an appearance similar to silk. [8] Plissé is chemical finish in which the fabrics are treated with sodium hydroxide to obtain a puckering effect. [9] Deweighting, or weight reduction, is a treatment for polyester to make it like silk. The treatment peels the surface and reduces the fiber ...
Solidification shrinkage occurs because metals are less dense as a liquid than a solid, so during solidification the metal density dramatically increases. Patternmaker's shrinkage refers to the shrinkage that occurs when the material is cooled from the solidification temperature to room temperature, which occurs due to thermal contraction. [20]
A bronze casting showing the sprue and risers. A riser, also known as a feeder, [1] is a reservoir built into a metal casting mold to prevent cavities due to shrinkage.Most metals are less dense as a liquid than as a solid so castings shrink upon cooling, which can leave a void at the last point to solidify.
Directional solidification can be used as a purification process. Since most impurities will be more soluble in the liquid than in the solid phase during solidification, impurities will be "pushed" by the solidification front, causing much of the finished casting to have a lower concentration of impurities than the feedstock material, while the ...
Curing is a chemical process employed in polymer chemistry and process engineering that produces the toughening or hardening of a polymer material by cross-linking of polymer chains. [1] Even if it is strongly associated with the production of thermosetting polymers , the term "curing" can be used for all the processes where a solid product is ...
The process produces a tougher, more ductile material, and eliminates columnar grains and dendritic segregation that sometimes occurs during casting. Normalizing improves machinability of a component and provides dimensional stability if subjected to further heat treatment processes.