Direct reduction processes can be divided roughly into two categories: gas-based and coal-based. In both cases, the objective of the process is to remove the oxygen contained in various forms of iron ore (sized ore, concentrates, pellets, mill scale, furnace dust, etc.) in order to convert the ore to metallic iron, without melting it (below 1,200 °C (2,190 °F)).
In the iron and steel industry, direct reduction is a set of processes for obtaining iron from iron ore, by reducing iron oxides without melting the metal. The resulting product is pre-reduced iron ore. Historically, direct reduction was used to obtain a mix of iron and slag called a bloom in a bloomery.
The sponge iron reaction (SIR) is a chemical process based on redox cycling of an iron-based contact mass, the first cycle is a conversion step between iron metal (Fe) and wuestite (FeO), the second cycle is a conversion step between wuestite (FeO) and magnetite (Fe 3 O 4). [1]
Direct reduction is the result of blending carbon with iron oxide ore, heating the mixture, removing the sponge iron from the carbon, grinding it, annealing it, and regrinding to make the powder form usable for manufacturing. Gas atomization occurs when a molten metal is passed through a passageway to a gas-filled chamber that cools the metal.
A bloomery is a type of metallurgical furnace once used widely for smelting iron from its oxides. The bloomery was the earliest form of smelter capable of smelting iron. Bloomeries produce a porous mass of iron and slag called a bloom. The mix of slag and iron in the bloom, termed sponge iron, is usually consolidated and further forged into ...
The HIsarna ironmaking process is a direct reduced iron process for iron making in which iron ore is processed almost directly into liquid iron ().The process combines two process units, the Cyclone Converter Furnace (CCF) for ore melting and pre-reduction and a Smelting Reduction Vessel (SRV) where the final reduction stage to liquid iron takes place.
Direct reduction is the fraction of iron oxide reduction that occurs in a blast furnace due to the presence of coke carbon, while the remainder - indirect reduction - consists mainly of carbon monoxide from coke combustion. It should also be noted that many non-ferrous oxides are reduced by this type of reaction in a blast furnace.
The company was founded in 1797 as a coal mine by Count Eric Ruuth. [2] It also made refractory and salt glazed ceramics. [3]In the early 20th century, Höganäs developed the Höganäs Method, considered the most effective method of producing sponge iron powder by reducing iron ore with coke, lime, and clay. [4]