Machinability is the ease with which a metal can be cut permitting the removal of the material with a satisfactory finish at low cost. [1] Materials with good machinability (free machining materials) require little power to cut, can be cut quickly, easily obtain a good finish, and do not cause significant wear on the tooling.
The machinability rating of a material attempts to quantify the machinability of various materials. It is expressed as a percentage or a normalized value. The American Iron and Steel Institute (AISI) determined machinability ratings for a wide variety of materials by running turning tests at 180 surface feet per minute (sfpm). It then ...
In 200 series stainless steels the structure is obtained by adding manganese and nitrogen, with a small amount of nickel content, making 200 series a cost-effective nickel-chromium austenitic type stainless steel. 300 series stainless steels are the larger subgroup. The most common austenitic stainless steel and most common of all stainless ...
SAE Type 630 stainless steel (more commonly known as 17-4 PH, or simply 17-4; also known as UNS S17400) is a grade of martensitic precipitation hardened stainless steel. It contains approximately 15–17.5% chromium and 3–5% nickel, as well as 3–5% copper. [1] The name comes from the chemical makeup which is approximately 17% chromium and 4 ...
440 series has three types: 440A, 440B, and 440C. 440A is a relatively low-cost, highly corrosion-resistant stainless steel. In China, A honest Changjiang Stainless Steel developed 7Cr17MoV, a modified 440A, by adding more Vanadium. [34] 440B is almost identical to 440A but has a higher carbon content range compared to 440A.
AL-6XN (UNS designation N08367) is a type of weldable stainless steel that consist of an alloy of nickel (24%), chromium (22%) and molybdenum (6.3%) with other trace elements such as nitrogen. The high nickel and molybdenum contents of the AL-6XN alloy give it good resistance to chloride stress- corrosion cracking.
Download as PDF; Printable version; ... 4340 steel is an ultra-high strength steel classified a ... The machinability of 4340 steel in the annealed condition is rated ...
The SAE steel grades system is a standard alloy numbering system (SAE J1086 – Numbering Metals and Alloys) for steel grades maintained by SAE International.. In the 1930s and 1940s, the American Iron and Steel Institute (AISI) and SAE were both involved in efforts to standardize such a numbering system for steels.