The design of an extrusion profile has a large impact on how readily it can be extruded. The maximum size for an extrusion is determined by finding the smallest circle that will fit around the cross-section, this is called the circumscribing circle. This diameter, in turn, controls the size of the die required, which ultimately determines if ...
In steel extrusions, the depth of an indentation should be no greater than its width at its narrowest point. This is necessary to provide sufficient strength in the tongue portion of the extruding die. In copper alloys, magnesium, and aluminum, the depth of an indentation may be greater since extrusion pressures are lower.
Examples of T-slotted profiles 1964 patent demonstrating early use of extruded T-slot members. Cross-section of 80/20 T-slotted profiles, 10 and 15 series A bicycle trailer for bike-trekking with three Euroboxes and aluminium profile framing
6061 is an alloy used in the production of extrusions—long constant–cross-section structural shapes produced by pushing metal through a shaped die. Cold and Hot Stamping. 6061 sheet in the T4 condition can be formed with limited ductility in the cold state.
Extrusion is a plastic deformation process in which raw material (billet) is forced to flow by compression through the die opening of a smaller cross-section area. The extrusion process is divided in two basic types: direct extrusion and indirect extrusion.
T1 temper 6063 has an ultimate tensile strength of at least 120 MPa (17,000 psi) in thicknesses up to 12.7 mm (0.5 in), and 110 MPa (16,000 psi) from 13 to 25 mm (0.5 to 1 in) thick, and yield strength of at least 62 MPa (9,000 psi) in thickness up to 13 millimetres (0.5 in) and 55 MPa (8,000 psi) from 13 mm (0.5 in) thick.